摘要
为了分析溶损反应动力学行为对焦炭反应后强度的影响,在1 050℃～1 300℃的范围内,对三种典型焦炭进行了等温溶损反应实验.当焦炭的溶损失重率为25%时停止反应,通过I型转鼓检测焦炭的溶损后强度.结果表明,不同反应性的焦炭发生最严重的劣化梯度反应时的温度不同,高反应性焦炭为1 100℃左右,低于其他两种焦炭.虽然高反应性焦炭发生最严重的劣化梯度反应后的强度很低,但改变反应温度使反应速率加快或减慢都能使高反应性焦炭的反应后强度显著地提高.
In order to clarify the solution loss kinetics behavior on coke strength after re- action, three representative cokes were used for solution loss reaction experiment. Isothermal reaction between coke and CO2 at 1 050 ℃-1 300℃C was stopped at a weight loss of 25%, and the strength of coke was tested by I type drum. The results showed that the temperature of gradient reaction brings the most serious degradation to three cokes were different due to different reactivity, and the temperature of the high reactive coke is about 1 100℃ which is lower than another two cokes. Although the strength of high reactive coke after gradient reaction of most serious degradation is poor, reaction rate is accelerated or declined by changing reaction temperature, post-reaction strength of high reactive coke increased markedly.
出处
《煤炭转化》
CAS
CSCD
北大核心
2012年第2期12-16,共5页
Coal Conversion
基金
国家自然科学基金资助项目(50974071)
关键词
焦炭
反应后强度
温度
溶损反应
coke, post-reaction strength, temperature, solution loss reaction