管道弯头爆裂失效分析 被引量:8

Failure Analysis of Pipe Elbow Cracking
下载PDF
导出
摘要 对粗混胺工艺管道弯头爆裂处,通过宏观检查弯头裂口外观、测厚检查弯头减薄、化学分析弯头化学成分变化等情况,分析了弯头爆裂失效的原因。结果表明:介质对管壁长时间腐蚀及介质流动对弯头冲刷造成管壁减薄是粗混胺工艺管道失效的原因。文中的分析给工艺管道的设计和管理提供了可靠的依据,避免同类事故的再次发生,确保化工生产安全经济运行。 This paper analyzes the causes of failure of pipe elbow cracking by macroscopic checking of the appearance of elbow cracks,by thickness checking of the elbow thinning and by chemical analyzing of the changes of elbow chemical components etc in places with coarse mixed amine process pipe elbow cracks.The results show that the reasons of coarse mix amine process pipe failure were long-term pipe wall corrosion by media and the thinning of pipe wall because of elbow flush by medium flow,which provides a reliable basis for process pipe design and management,avoiding similar accidents form happening again,and ensuring the chemical production safely and economically.
出处 《管道技术与设备》 CAS 2012年第2期56-57,共2页 Pipeline Technique and Equipment
关键词 弯头 腐蚀 磨损 爆裂 介质 elbow corrode wear cracking medium
  • 相关文献

参考文献1

二级参考文献5

  • 1SH3408-1996,钢制对焊无缝管件[S].
  • 2GB/T8163-1999.输送流体用无缝钢管[S].[S].,..
  • 3GB/T699-1999,优质碳素结构钢[S].
  • 4GB 3087-1999,低中压锅炉用无缝钢管[S].
  • 5郭林栋.热推弯头的生产[J].鞍钢技术,1992(7):26-31. 被引量:2

共引文献3

同被引文献41

引证文献8

二级引证文献61

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部