摘要
The effects of Y addition on the structural and mechanical properties of CuZrAl bulk metallic glass（BMG） were studied.The results show that the glass forming ability of CuZrAl system is improved by the addition of Y and the fracture strength decreases with Y addition due to the reduction of binding energy induced by Y.The fracture surface is dominated by vein-like patterns in Cu45Zr48Al7 bulk metallic glass,and changes to smooth regions in Cu46Zr42Al7Y5 BMG.TEM observation shows that Cu45Zr48Al7 BMG has a composite microstructure of nanocrystalline phases dispersed in amorphous matrix.However,the Cu46Zr42Al7Y5 BMG shows a fully amorphous structure.
研究添加Y元素对CuZrAl块体金属玻璃的结构和力学性能的影响。结果表明,添加Y元素提高CuZrAl体系的玻璃形成能力,而且由于添加Y元素可以降低该体系的结合能,从而降低其断裂强度。Cu45Zr48Al7块体金属玻璃的断裂表面主要呈脉状,而Cu46Zr42Al7Y5块体金属玻璃的断裂表面则很平滑。TEM观察表明,Cu45Zr48Al7的微观结构为非晶基体中含有纳米相,然而Cu46Zr42Al7Y5块体金属玻璃为全非晶结构。