镁对La_(1-x)Mg_xNi_(2.5)Co_(0.5)(x=0~0.4)合金循环过程中电化学性能的影响

Effect of Magnesium Content on Electrochemical Properties of La_(1-x)Mg_xNi_(2.5)Co_(0.5)(x=0~0.4) Hydrogen Storage Alloys
原文传递
导出
摘要 采用充放电测试、高倍率放电等方法,系统分析了Mg对合金在循环过程中的电化学性能影响规律,结果表明La1-xMgxNi2.5Co0.5(x=0~0.4)合金在初始阶段的高倍率放电性能随着Mg含量的增加先增大后减小,La1-xMgxNi2.5Co0.5(x=0~0.4)合金经90次循环后的放电容量保持率先从x=0时的28.0%增加到x=0.2时的59.1%,然后下降到x=0.4时的45.7%。 The electrochemical properties of La1-xMgxNi2.5Co0.5(x=0~0.4) alloys were investigated using charge and discharge testing and HRD testing methods.The results showed that the degradation extent of HRDs was different during cycles,which was ascribed to the corrosion and surface resistance of the alloys with the increase of cycles.The cycle stability of the alloy electrodes first increased from 28.0%(x=0) to 59.1%(x=0.2),then decreased to 45.7%(x=0.4) after 90 charge/discharge cycles.
出处 《中国稀土学报》 CAS CSCD 北大核心 2012年第3期380-384,共5页 Journal of the Chinese Society of Rare Earths
基金 稀土资源利用国家重点实验室开放课题基金(RERU2011010)资助
关键词 AB3型储氢合金 La-Mg-Ni 电化学性能 稀土 AB3 type hydrogen storage alloy La-Mg-Ni electrochemical properties rare earths
  • 相关文献

参考文献5

二级参考文献75

共引文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部