纳米氧化锆水悬浮液的稳定性 被引量:2

Stability of Nano-Sized Zirconia Aqueous Suspensions
原文传递
导出
摘要 通过黏度、表面张力、密度及粒度测试等手段研究了球磨剂、球磨时间、pH值、添加剂等因素对纳米氧化锆水悬浮液稳定性的影响。结果表明:球磨时间2h,球磨剂与氧化锆质量比为3.5%,添加剂可用乙二醇,悬浮液pH值为10.0,氧化锆粒径小于15nm时,纳米氧化锆水悬浮液可稳定30天。 Influences of the factors including ball mill agent,ball-milling time,value of pH and additive on the stability of nano-sized zirconia aqueous suspensions were investigated by viscosity,surface tension,density and granularity test means.The results showed that when ball-milling time was 2h,mass ratio of ball mill agent to zirconia was 3.5%,stabilizer was glycol,pH value of suspensions was 10.0,granularity of zirconia was less than 15nm,nano-sized zirconia aqueous suspensions can be stable for 30 days.
出处 《光谱实验室》 CAS CSCD 2012年第3期1588-1591,共4页 Chinese Journal of Spectroscopy Laboratory
基金 2007辽宁省纳米技术及系统重点实验室开放项目(2007-5)
关键词 纳米氧化锆 水悬浮液 稳定性 Nano-Zirconia Aqueous Suspension Stability
  • 相关文献

参考文献2

二级参考文献20

  • 1Lange F F. J Am Ceram Soc, 1989, 72 (1): 3-15.
  • 2Cesarano J, Aksay I A. J Am Ceram Soc, 1988, 71 (4): 250--255.
  • 3Sigmund W M, Bell N S, Bergstrom L. J Am Ceram Soc, 2000, 83 (7): 1557-1574.
  • 4Jean J H, Wang H R. J Am Geram Soc, 2000, 83 (2): 277-280.
  • 5Davies J, Binner J G P. J Eur Ceram Soc, 2000, 20: 1539-1553.
  • 6Liu Y Q, Gao L, Sun J .J Eur Ceram Soc, 2002, 22 (6): 863-871.
  • 7Kuo P L, Chang T C, Lu L M. J Appl Polymer Sci, 1992, 44: 859--867.
  • 8Guo L, Zhang Y. J Am Ceram Soc, 1998, 81 (3): 549-556.
  • 9Fagerholm H B, Mikkola P, Rosenholm J B. J Eur Ceram Soc, 1999, 19: 41-48.
  • 10Hoffman R L. MRS Bulletin, 1991, 8: 32-37.

共引文献20

同被引文献25

引证文献2

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部