α-磷酸三钙/HA晶须/羧甲基壳聚糖-明胶复合增强多孔骨水泥的制备研究 被引量:3

Preparation of α-Tricalcium Phosphate/HA Whisker/Carboxymethyl Chitosan-Gelatin Composite Porous Bone Cement
原文传递
导出
摘要 为研究羟基磷灰石(HA)晶须和羧甲基壳聚糖-明胶(CMC-Gel)对多孔磷酸钙骨水泥(CPC)力学性能的影响,将α-磷酸三钙(α-TCP)粉、HA晶须和致孔剂L-谷氨酸钠按一定的质量比进行混合,加入调和液制备成α-TCP/HA晶须复合多孔骨水泥,然后将其浸润到一系列不同CMC和Gel质量比的溶液中以制备α-TCP/HA晶须/CMC-Gel复合增强多孔骨水泥,对其进行抗压强度测试和扫描电镜观察。结果显示,当HA晶须含量为4%,未添加CMC和Gel时,α-TCP/HA晶须复合多孔骨水泥的抗压强度达到2.57MPa,与未复合HA晶须的骨水泥相比提高了81%;当CMC和Gel的质量比为50∶50时,α-TCP/HA晶须/CMC-Gel复合多孔骨水泥的抗压强度达到最大值3.34MPa,与单纯的多孔α-TCP骨水泥相比提高了135%,同时韧性也有较大改善。 In order to investigate the effects of HA whisker and carboxymethyl chitosan-gelatin(CMC-Gel) on the mechanical properties of porous calcium phosphate cement, a series of α-tricalcium phosphate (α-TCP), HA whisker and L-sodium glutamate porogen with different mass fractions were mixed, and setting liquid was added to them to prepare α-TCP/HA whisker composite porous bone cement. Then, the cement was immersed in a series of CMC-Gel solutions which had different weight ratios of CMC to Gel to prepare α-TCP/HA whisker/CMC-Gel composite porous bone cement. The compressive strengths and microstructure of cement were characterized by mechanical testing machine and SEM. The results showed that when the mass fraction of HA whisker is 40/'60, the compressive strength of α-TCP/HA whisker composite porous bone cement reaches 2.57MPa, which is 1.81 times that of a-TCP bone cement. When the weight ratio of CMC to Gel is 50 : 50, the compressive strength of α-TCP/HA whisker/CMC-Gel composite porous bone cement is 3.34MPa, which is 2.35 times that of a-TCP bone cement, and the toughness of the composite cement is greatly improved as well.
出处 《生物医学工程学杂志》 EI CAS CSCD 北大核心 2012年第3期491-495,共5页 Journal of Biomedical Engineering
关键词 磷酸钙骨水泥 HA晶须 羧甲基壳聚糖-明胶 增强 Calcium phosphate cement (CPC) HA whisker Carboxymethyl chitosan-gelatin (CMC-Gel) Rein- forcement
  • 相关文献

参考文献15

二级参考文献138

共引文献100

同被引文献39

  • 1王彦伟,蔡舒,姚康德.明胶溶胀行为对自固化多孔骨水泥性能和结构的影响[J].生物骨科材料与临床研究,2003,1(1):41-42. 被引量:1
  • 2潘朝晖,范清宇,蔡和平,马保安,黄波,姜林莉,文艳华.明胶对自固化磷酸钙骨水泥性能的影响[J].医学研究生学报,2005,18(8):696-699. 被引量:2
  • 3田一平,杨建华,李晖,郭灵虹.影响α-TCP和HA生物陶瓷表面形成类骨磷灰石的形貌、结构的因素研究[J].四川大学学报(自然科学版),2007,44(1):135-140. 被引量:1
  • 4VARALAKSHMI PR,KAVITHA M,GOVINDAN R,et al.Effect of statins withα-tricalcium phosphate on proliferation,differentiation,and mineralization of human dental pulp cells.J Endod,2013,39(6):806-812.
  • 5MARUKAWA K,UEKI K,OKABE K,et al.Use of selfsettingα-tricalcium phosphate for maxillary sinus augmentation in rabbit.Clin Oral Implants Res,2011,22(6):606-612.
  • 6ROJBANI H,NYAN M,OHYA K,et al.Evaluation of the osteoconductivity ofα-tricalcium phosphate,β-tricalcium phosphate,and hydroxyapatite combined with or without simvastatin in rat calvarial defect.J Biomed Mater Res A,2011,98(4):488-498.
  • 7VARALAKSHMI PR,KAVITHA M,GOVINDAN R,et al.Effect of statins withα-tricalcium phosphate on proliferation,differentiation,and mineralization of human dental pulp cells.J Endod,2013,39(6): 806-812.
  • 8BIGI A,PANZAVOLTA S,RUBINI K.Relationship between triple-helix content and mechanical properties of gelatin films.Biomaterials,2004,25(25):5675-5680.
  • 9TOUNY AH,LAURENCIN C,NAIR L,et al.Formation of composites comprised of calcium deficient HAp and crosslinked gelatin.J Mater Sci:Mater Med,2008,19(10):3193-3201.
  • 10KUIJPERS AJ,ENGBERS GH,KRIJGSVELD J,et al.Cross-linking and characteri sterisation of gelatin matrices for biomedical applications.Biomater Sci Polym Ed,2000,11(3):225-243.

引证文献3

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部