电气石/La/TiO2光催化材料的合成与表征

Preparation and characterization of tourmaline/La/TiO_2 photocatalyst materials
原文传递
导出
摘要 以硝酸镧、天然电气石(Tourmaline,简称T)和钛酸丁酯为原料,采用溶胶-凝胶法制备掺杂电气石和稀土La的TiO2复合光催化薄膜样品。用正交试验方法对影响该薄膜样品光催化性能的制备工艺进行优化,并通过紫外可见光谱对复合薄膜样品的吸收光谱进行分析。结果表明,掺杂稀土元素La可使TiO2的光吸收范围发生红移,掺杂电气石将增强La/TiO2光吸收强度,T/La/TiO2复合光催化薄膜最佳制备工艺为:La3+掺杂量为1.2%(wt,下同)、电气石掺杂量为0.8%、焙烧温度为500℃、焙烧时间为1.5h、负载次数2次,样品的的甲醛降解率可达82.5%。 The composite film samples were prepared by using the sol-get method with lanthanum nitrate, natural tourmaline and tetrmn-butyl titanate as raw materials. The preparation technology of the film was analyzed using UV-Vis adsorption spectrum after optimized by orthogonal test. The results showed that the adsorption spectrum of TiO2 showed a gradual Einstein shift with the doping of lanthanum,and the absorbing intensity of TiO2 were enhanced with the doping of tourmaline. The optimal conditions were obtained: calcinated for 1.5h at 500℃ after load 2 times, the concentration of Laa+ and tourmaline in specimen were 1.2wt% and 0. 8wt%, respectively, and the degradation of formaldehyde of sample was 82.5%.
出处 《化工新型材料》 CAS CSCD 北大核心 2012年第6期69-71,共3页 New Chemical Materials
基金 广西研究生教育创新计划项目资助(2010106020830M58) 广西环境工程与保护评价重点实验室平台建设经费(09-007-07)
关键词 T/La/TiO2 光催化 正交试验 甲醛 tourmaline/La/TiO2,photocatalyst,orthogonal test,formaldehyde
  • 相关文献

参考文献11

二级参考文献58

共引文献110

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部