摘要
A new Nylon 11（PA11）/polyethylene-octene（POE） blends compatibilized by maleic anhydride grafted mixture polyethyleneocten（POE-g-MAH） was prepared through melt blending method.The isothermal crystallization kinetics and melting behaviors of PA11/POE blends were investigated in detail by differential scanning calorimetry（DSC） and polarized optical microscope.The n values of PA11 blending with POE or POE-g-MAH are almost similar with pure PA11,which indicates that the effect of POE and POE-g-MAH on nucleation and growth of PA11 crystal is slight.The overall crystallization rate of PA11/POE blends are higher than ones of pure PA11 at the same crystallization temperatures,but they decrease significantly when POE-g-MAH is added into PA11/POE blends.DSC heating curves of both PA11 and its blends exhibit two melting peaks,but the two melting peak become weaker when POE-g-MAH is add into PA11/POE blend systems.And the spherulite size is reduced significantly by the addition of POE-g-MAH compared with pure PA11 and PA11/POE blends.
A new Nylon 11（PA11）/polyethylene-octene（POE） blends compatibilized by maleic anhydride grafted mixture polyethyleneocten（POE-g-MAH） was prepared through melt blending method.The isothermal crystallization kinetics and melting behaviors of PA11/POE blends were investigated in detail by differential scanning calorimetry（DSC） and polarized optical microscope.The n values of PA11 blending with POE or POE-g-MAH are almost similar with pure PA11,which indicates that the effect of POE and POE-g-MAH on nucleation and growth of PA11 crystal is slight.The overall crystallization rate of PA11/POE blends are higher than ones of pure PA11 at the same crystallization temperatures,but they decrease significantly when POE-g-MAH is added into PA11/POE blends.DSC heating curves of both PA11 and its blends exhibit two melting peaks,but the two melting peak become weaker when POE-g-MAH is add into PA11/POE blend systems.And the spherulite size is reduced significantly by the addition of POE-g-MAH compared with pure PA11 and PA11/POE blends.