含Si–O–C界面层的C/Si–C–N复合材料的抗氧化性能(英文) 被引量:2

Oxidation Resistance of C/Si-C-N Composite with Si-O-C Interlayer
原文传递
导出
摘要 为了研究利用Si–O–C界面层来提高碳纤维增强陶瓷基复合材料的抗氧化性能,利用化学气相浸渗和聚合物浸渗裂解工艺制备了以Si–O–C为界面的碳纤维增强Si–C–N陶瓷基复合材料(C/Si–O–C/Si–C–N)和无界面层的碳纤维增强Si–C–N陶瓷基复合材料(C/Si–C–N)。研究了C/Si–O–C/Si–C–N和C/Si–C–N在600、900℃和1 200℃空气环境中的氧化行为。结果表明:采用Si–O–C界面层后可提高复合材料的抗氧化性能;Si–O–C界面层较高的氧化抗力是碳纤维增强Si–C–N复合材料抗氧化性能提高的主要原因。 In order to improve oxidation resistance of carbon fiber reinfbrced ceramic matrix composites, a carbon fiber reinforced Si-C-N matrix composite with a Si-O-C interlayer (C/Si-O-C/Si-C-N) was fabricated via chemical vapor infiltration and polymer impregnation and pyrolysis process. The oxidation behaviors of the C/Si-O-C/Si-C-N and the carbon fiber reinforced Si-C-N com- posite without interphase (C/Si-C-N) were investigated in air at 600, 900 and 1 200℃, respectively. The results indicate that the oxidation resistance of C/Si-O-C/Si-C-N is improved by Si-O-C interphase compared to C/Si-C-N. The higher oxidation resistance of C/Si-O-C/Si-C-N is attributed to the higher inoxidizability of Si-O-C interlayer.
作者 卢国锋
出处 《硅酸盐学报》 EI CAS CSCD 北大核心 2012年第8期1169-1173,共5页 Journal of The Chinese Ceramic Society
基金 国家自然科学基金(50772089) 陕西省军民融合基金(11JMR-03) 渭南师范学院科研基金(11YKP018)
关键词 碳纤维 陶瓷基复合材料 硅氧碳界面 carbon fibre ceramic-matrix composites silicon oxycarbide interlayer
  • 相关文献

参考文献1

二级参考文献2

共引文献3

同被引文献14

引证文献2

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部