Vacuum brazing of Si/SiC ceramic composite and Invar alloy using TiSOCu-W filler metals 被引量:2

Vacuum brazing of Si/SiC ceramic composite and Invar alloy using TiSOCu-W filler metals
下载PDF
导出
摘要 Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope (SEM) and energy dispersive spectrometer (EDS). The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature. Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope (SEM) and energy dispersive spectrometer (EDS). The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature.
出处 《China Welding》 EI CAS 2012年第1期76-80,共5页 中国焊接(英文版)
关键词 Si/SiC ceramic composite lnvar alloy BRAZING Ti50Cu-W filler metals Si/SiC ceramic composite, lnvar alloy, brazing, Ti50Cu-W filler metals
  • 相关文献

参考文献10

  • 1Jonas K B, Yano T K, Iseki T K. Brazing of pressureless sinlered SiC using Ag-Cu-Ti alloy. Journal of Materials Science, 1987, 22 ( 7 ) : 2431 - 2434.
  • 2Fujio T M,Naka M.Microstructure of interface of SiC/Cu-Ag-Ti/Cu.Proceeding of Designing of Interfacial Structures in Advanced Materials and Their Joints,2002 : 634 - 639.
  • 3Iseki T,Kameda T,Maruyama T.Interfacial reactions between SiC and aluminum during joining.Journal of Materials Science, 1984, 19(5): 1692-1698.
  • 4Shigeo U, Maeda K, Nakade S. Brazing of SiC with Cu-Sn-Ti-A1 filler metal. Proceeding of Designing of lnterfacial Structures in Advanced Materials and Their Joints, 2002: 640 - 644.
  • 5Raymundo A, Thomas W. Metal substrate effects on the thermal chemistry active brazing interfaces. Acta Materialia, 2003, 51(16) : 4871 -4879.
  • 6Ferro A C, Derby B. Liquid phase bonding of siliconized silicon carbide. Journal of Materials Science, 1995, 30 (24) : 6119 -6135.
  • 7Liu H J. Interface structure and formation mechanism of diffusion-bonded joints of SiC ceramic to TiAl-based alloy. Scripta Materialia, 2000, 43 ( 1 ) : 49 - 53.
  • 8Lino Y. Partial transient liquid-phase metals layer technique of ceramic-metal bonding. Journal of Materials Science, 1990, 9(10) : 104 - 106.
  • 9Singh M. Microstructure and mechanical properties of reaction-formed joint in reaction-bonded silicon carbide ceramic. Journal of Materials Science, 1998, 33 (24) : 5781 - 5789.
  • 10Lee H K, Hwang S H, Lee J Y. Effects of the relative contents of silver and copper on the inteffacial reaction and bonded strength in the active brazing of SiC. Journal of Materials Science, 1993, 28(7) : 1765 - 1774.

同被引文献8

引证文献2

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部