弹性体和刚性粒子对聚甲醛的增韧改性研究 被引量:14

Study on Toughening Modification of POM with Elastomers and Rigid Particles
下载PDF
导出
摘要 采用热塑性聚氨酯弹性体(TPU)和刚性粒子纳米二氧化硅(SiO2)对聚甲醛(POM)进行了协同增韧,并通过差示扫描量热仪和扫描电子显微镜等分析了增韧体系的结构和性能。结果表明,TPU/SiO2协同增韧提高了POM缺口冲击强度,且能有效降低传统增韧方法对材料拉伸强度和弯曲模量造成的损失;当POM中单独加入20%(质量分数,下同)TPU时,POM的缺口冲击强度提高了89%,拉伸强度和弯曲模量却分别降低了18%和40%;单独加入2%SiO2时,POM的缺口冲击强度仅提高22%,增韧效果不明显;同时加入20%的TPU和2%的SiO2时,POM的缺口冲击强度提高了230%,拉伸强度和弯曲模量仅分别下降了8%和13%。 The synergetic toughening effect of TPU and nano-Si02 on POM was investigated in this paper. The structure of the toughened system was characterized using DSC and SEM. When 20% TPU was incorporated into POM alone, the notched impact strength was 89 % higher than that of neat POM, but the tensile strength and flexural modulus were lowered by 18% and 40 %, respectively; When 2% SiO2 was added to POM, the increase in notched impact strength was only 22%. When 20% TPU and 2% SiO2 were incorporated into POM, the notched impact strength was 230% higher than that of POM, and the tensile strength and flexural modulus were 8% and 13% lower, respectively.
出处 《中国塑料》 CAS CSCD 北大核心 2012年第8期26-30,共5页 China Plastics
关键词 聚甲醛 热塑性聚氨酯弹性体 纳米二氧化硅 增韧 改性 polyoxymethylene thermoplastic polyurethane nano-silia toughening modification
  • 相关文献

参考文献17

  • 1庞绍龙,林桂芳.工程塑料聚甲醛的生产及其应用研究[J].化学工程与装备,2010(3):120-122. 被引量:19
  • 2Guhanathan S, Saroja Devi M. Physicochemical Characterization of the Filler Matrix Interface in Elastomer encapsulated Fly Ash/Polyester Particulate Composites[J]. Journal of Applied Polymer Science, 2005, 97(1):171-175.
  • 3Lehmann B, Friedrich K. Improvement of Notch Toughness of Low Nano SiO2 Filled Polypropylene Composites [J]. Jouranal Materials Science letters, 2004, 22: 1027- 1031.
  • 4刘莉,徐开杰.聚甲醛改性研究现状[J].工程塑料应用,2008,36(2):71-75. 被引量:37
  • 5朱勇平,王炼石,付锦锋.弹性体增韧POM的研究进展[J].塑料,2008,37(6):73-76. 被引量:12
  • 6Pielichowski K, Leszczynska A. Structure-property Relationships in Polyoxymethylene/Thermoplastic Polyurethane Elaslomer Blends[J]. J Polym Eng, 2005, 25: 3596-3599.
  • 7Gryaznov V G, Trusov I. I. Size Effects in Micromechanics of Nanocrystals[J]. Progress in Materials Science, 1993,37:289-293.
  • 8张辉.弹性体与纳米SiO2改性聚甲醛的研究[D].成都:四川大学高分子科学与工程学院,2009.
  • 9于建,王书武,黄国峰.NBR对POM树脂的增韧行为[J].高分子材料科学与工程,2000,16(1):109-112. 被引量:26
  • 10徐卫兵,朱士旺,蔡琼英.尼龙—12增韧改性聚甲醛的研究[J].工程塑料应用,1995,23(1):9-11. 被引量:9

二级参考文献76

共引文献120

同被引文献183

引证文献14

二级引证文献47

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部