摘要
The influence of silane coupling agent on the film forming of galvanized steel treated with cerium salt was studied by scanning electron microscopy （SEM） and X-ray photoelectron spectroscopy （XPS）, and the corrosion resistance of conversion films was analyzed by electro interstitial scanning （EIS）. The results show that silane coupling agent KH-570 has significant influence on the compactness and homogeneity of cerium conversion films, and the process of film forming is promoted by increasing the content of tervalent and tetravalent cerium oxide. The impedance value of the cerium conversion film, especially modified with KH-570, is greater than that of the base metal, which reveals that it is necessary to add silane coupling agent to the film-forming solution in order to improve the corrosion resistance of the conversion film.
The influence of silane coupling agent on the film forming of galvanized steel treated with cerium salt was studied by scanning electron microscopy （SEM） and X-ray photoelectron spectroscopy （XPS）, and the corrosion resistance of conversion films was analyzed by electro interstitial scanning （EIS）. The results show that silane coupling agent KH-570 has significant influence on the compactness and homogeneity of cerium conversion films, and the process of film forming is promoted by increasing the content of tervalent and tetravalent cerium oxide. The impedance value of the cerium conversion film, especially modified with KH-570, is greater than that of the base metal, which reveals that it is necessary to add silane coupling agent to the film-forming solution in order to improve the corrosion resistance of the conversion film.