利用先末端氯硅烷化线形活性阴离子聚丁二烯,然后水解的方法合成了聚丁二烯/二氧化硅(PB/SiO2)杂化材料,采用红外光谱、GPC和TG分析了PB/SiO2杂化材料的结构及性能,并用激光粒度仪、TEM、HRTEM分析了PB/SiO2杂化材料的微相结构,最后对合成PB/SiO2杂化材料的影响因素进行了研究。结果表明:合成的PB/SiO2杂化材料是具有核壳结构纳米尺寸的颗粒,颗粒尺寸在100 nm左右;延长反应时间、减小聚丁二烯分子量及减小SiCl4加入量可使产物中PB/SiO2杂化材料的摩尔分数增加;H2O与—Cl的物质的量之比为2时,产物中PB/SiO2杂化材料的摩尔分数最大。
Core-shell polybutadiene/silica （PB/silica） hybrid nanoparticles have been synthesized by hydrolysis of chlorosilane-functionalized PB synthesized by anionic polymerization techniques. The structure and properties of the PB/silica hybrid material were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis and gel permeation chromatography. The microstructure of the PB/silica hybrid material was characterized by laser diffraction particle size analysis, transmission electron microscopy and high resolution transmission electron microscopy. The factors that affect the properties of the product such as reaction time, molecular weight of PB, and the amounts of SiC14 and H20 were varied. The results indicated that the size of the nanoparticles was about 100 nm, and the content of PB/silica hybrid nanoparticles in the product increased with increasing reaction time and with decreasing molecular weight of PB, and on reducing the amount of SiCI4. When the molar ratio n（ H20）/n（ CI ） was 2, the content of PB/silica hybrid nanoparticles in the product was found to be a maximum.
出处
《北京化工大学学报（自然科学版）》
CAS
CSCD
北大核心
2012年第5期53-58,共6页
Journal of Beijing University of Chemical Technology(Natural Science Edition)
基金
国家自然科学基金(50773002/20934001)
关键词
末端氯硅烷化
水解
核壳结构
聚丁二烯/二氧化硅杂化材料
chlorosilane-functionalization
hydrolysis
core -shell structure
polybutadiene/silica hybrid nanoparticles