摘要
对一种含0.27%C的工程机械用低合金高强度耐磨钢NM500进行轧制及两相区热处理试验,研究了普通高温轧制+空冷、高温控制轧制+空冷、高温控制轧制+层流冷却以及低温控制轧制+层流冷却工艺参数对实验钢两相区热处理后力学性能和三体冲击磨料磨损性能的影响。结果表明,轧制及轧后冷却工艺参数对试验钢两相区热处理后的性能影响较大,低温控制轧制+层流冷却较好的细化了原始铁素体晶粒,在经过适当的两相区热处理后得到保留,有利于提高实验钢的低温冲击韧性和耐磨性能。
Effects of process parameters,such as conventional high temperature rolling and air cooling,high temperature controlled rolling and air cooling,high temperature controlled rolling and laminar cooling,low temperature controlled rolling and laminar cooling,on microstructure,mechanical property and three-body impact abrasive wear behavior of 0.27% C abrasion resistant steel NM500 heat-treated in two-phase region were investigated.The results show that rolling and cooling mode after rolling before the heat treatment presented significant influence on properties and wear behavior of the test steel.The prior ferrite grains were refined by low temperature rolling and laminar cooling,and the fine microstructure was retained after two-phase region heat treatment.The small amounts of fine ferrite were beneficial to improving toughness and wear-resisting property of the steel.
出处
《材料热处理学报》
EI
CAS
CSCD
北大核心
2012年第9期65-69,共5页
Transactions of Materials and Heat Treatment
基金
国家重点研究发展计划(973计划)项目(2010CB630801)
关键词
耐磨钢
工艺参数
两相区热处理
三体冲击磨料磨损
abrasion resistant steel
process parameter
two-phase region heat treatment
three-body impact-abrasive wear