低液固比体系高岭土微球原位合成Y沸石 被引量:5

Synthesis of Y zeolite via in situ crystallization on Kaolin microsphere with low H2O/microsphere weight ratio
下载PDF
导出
摘要 以高岭土微球为全部硅铝原料,经焙烧、碱抽提、水热处理等工艺,直接原位晶化合成了Y分子筛。扫描电镜分析表明:在高岭土微球上均匀生成了晶型完整、粒度为1μm左右的Y分子筛。结合X射线测试方法详细研究了体系硅铝比、碱度、碱抽提时间、导向剂构成及添加时间对Y分子筛合成的影响。研究表明:该水热反应体系的最佳配比为n(SiO2)/n(Al2O3)=10.0。反应适宜的碱度条件为:n(Na2O)/n(SiO2)=0.56,n(H2O)/n(Na2O)=35,碱度过高或过低都易有P杂晶生成。碱抽提过程对合成Y分子筛十分关键,最佳的抽提时间控制在12 h。导向剂构成为透明高清状,加入时间控制在碱抽提结束时最优,此时合成的Y分子筛品质最好。 Y zeolite was prepared by the hydrothermal method using Kaolin microspheres as the sole all silicon and alminum source.Scanning electron microscope analysis showed Y zeolite with the size of 1 μm.The influences of the n(SiO2)/n(Al2O3) molar ratio,alkali extraction,initial gel alkalinity,directing agent composition and addition time were discussed according to X-ray diffraction analysis.The optimum reaction system was n(SiO2)/n(Al2O3)=10.0,n(Na2O)/n(SiO2)=0.56,n(H2O)/n(Na2O)= 35.Higher or lower basicity would cause P phase emergence.The alkali extraction process was crucial to the synthesis of Y zeolite,and the optimal time was 12 h.The best quality Y zeolite could be obtained by controlling the addition time of the clear liquid directing agent at the end of alkali extraction.
机构地区 西北化工研究院
出处 《化工进展》 EI CAS CSCD 北大核心 2012年第10期2234-2238,共5页 Chemical Industry and Engineering Progress
基金 陕西省科技计划(2011K08-03) 陕西延长石油集团科技项目(ycsy2011ky-A-11)
关键词 高岭土微球 Y沸石 碱抽提 Kaolin microsphere zeolite Y alkali extraction
  • 相关文献

参考文献11

二级参考文献93

共引文献48

同被引文献43

引证文献5

二级引证文献17

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部