凝胶注模常温发泡制备氧化铝多孔陶瓷 被引量:18

Fabrication of porous alumina ceramics by gelcasting together with foaming at room temperature
下载PDF
导出
摘要 以高纯氧化铝为原料,通过起泡结合凝胶注模成型的方法制备了孔隙率为77%~85%、孔径为40~200μm的氧化铝多孔陶瓷.多孔陶瓷组成为α-Al2O3.多孔陶瓷的微结构可通过固含量与发泡剂加入量的改变进行调控.多孔陶瓷的耐压强度为9.40~32.50MPa,且对其断裂方式进行了研究.多孔陶瓷在1000℃下的热导率为0.80 W.(m.K)-1. Porous alumina ceramics with 77% -85% porosity and pore size of 40- 200 μm were fabricated by foaming together with gelcasting. The composition of porous ceramics was α-A12O3, and the microstructures were tailored by modulating the solid content or the quantity of foaming agent added. The compressive strengths were 9.40 - 32.50 MPa, and the fracture mode was studied. The thermal conductivity of porous ceramics was0.80 W ·(m·K) -1 at 1 000 ℃.
出处 《材料科学与工艺》 EI CAS CSCD 北大核心 2012年第4期144-148,共5页 Materials Science and Technology
基金 973项目(2010CB735810) 国家自然科学基金(51002145) 863计划项目(2009AA032503)
关键词 起泡法 凝胶注模 多孔陶瓷 耐压强度 热导率 porous ceramics foaming gelcasting compressive strengths thermal conductivity
  • 相关文献

参考文献17

  • 1Andre R. Studart, Urs T. Gonzenbach, Elena Tervoort, et al. Gauckler. Processing routes to macroporous ce- ramics : a review [ J ]. J. Am. Ceram. Soc. , 2006, 89 (6) :1771 - 1789.
  • 2P. Colombo, H. P. Degischer. Highly porous metals and ceramics [ J ]. Materials Science and Technology, 2010, 26(10) :1145 - 1158.
  • 3P. Colombo, Cekdar Vakifahmetoglu, Stefano Costacur- ta. Fabrication of ceramic components with hierarchical porosity [ J ]. J. Mater. Sci, 2010, 45 ( 20 ) : 5425 - 5455.
  • 4Paolo Colombo. In Praise of Pores [ J ]. Science, 2008, 322(5900) :381 - 383.
  • 5Santanu Dhara,Parag Bhargava. A Simple Direct Cast- ing Route to Ceramic Foams [ J ]. J. Am. Ceram. Soc. ,2003,86[ 10] :1645 -50.
  • 6Fa -Zhi Zhang, Takeaki Kato, Masayoshi Fuji, et al. Gelcasting fabrication of porous ceramics using a con- tinuous process [ J ]. Journal of the Europeam Ceramic Society, 2006,26 (4 - 5) : 667 - 671.
  • 7Xiaojian Mao, Shunzo Shimai, Shiwei Wang. Effects of Coarse Particles on the Gelcasting of Ceramic Foams [ J ]. J. Am. Ceram. Soc. ,2008,91 (7) :2412 - 2414.
  • 8Jana P, Ganesan V. Processing of low - density alumina foam[ J ]. J. Eur. Ceram. Soc., 2010, doi: 10. 1016/j. jeurceramsoc. 2010.07. 044.
  • 9Santanu Dhara, Parag Bhargava. A Simple Direct Cast- ing Route to Ceramic Foams [ J ]. J. Am. Ceram. Soc. , 2003,86 (10) :1645 -50.
  • 10Brent S. Murray. Stabilization of bubbles and foams [ J ]. Current Opinion in Colloid & Interface Science, 2007,12:232 - 241.

同被引文献149

引证文献18

二级引证文献100

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部