涂覆热分解与电化学聚合法制备聚苯胺/RuO_2复合电极材料 被引量:5

Polyaniline/RuO_2 composite electrode prepared by coating thermal decomposition and electrochemistry polymerization procedures
原文传递
导出
摘要 通过涂覆热分解法并结合电化学聚合法制备得到聚苯胺(PANI)/RuO2电极材料。使用涂覆热分解法于260℃热处理3h制备RuO2薄膜,通过电化学聚合法将PANI粒子沉积在RuO2薄膜上,并在80℃加热12h。采用XRD分析PANI/RuO2复合物晶相,采用SEM观察PANI/RuO2复合电极材料的形貌变化。利用循环伏安及恒流充放电测试了该复合电极的电化学性能。结果表明,PANI沉积时间为25min,该PANI/RuO2复合电极的最大电容量为9.72F,比电容为452F.g-1,充放电曲线体现了较低的电压降、等效串联电阻及良好的充放电性能。经1000次循环伏安后,其比电容损失约为11%。 Polyaniline (PANI)/RuO2 composite electrodes were prepared by coating thermal decomposition and electrochemistry polymerization procedures. RuO2 film was synthesized by coating thermal decomposition method at 260℃ for 3 h, and PANI particles were deposited on RuO2 films and dried at 80℃ for 12 h. The formation of the amorphous phase of PANI/RuO2 composite was studied by XRD. Morphologic variations of the composite electrodes were established by SEM. Electrochemical performances of the composite electrodes were measured by cyclic voltammetry (CV) and galvanostatic charge-discharge. The results show that when the deposition time of PANI is 25 min, the maximum capacitance and the specific capacitance of PANI/RuO2 composite electrode is 9.72 F and 452 F·g^-1 respectively. Charge-discharge curves of the composite electrodes illustrate low potential drops, internal resistances and good charge-discharge properties. Approximately 11% loss of capacitance is observed after 1000 CV cycles.
出处 《复合材料学报》 EI CAS CSCD 北大核心 2012年第5期1-5,共5页 Acta Materiae Compositae Sinica
基金 国家"863"高技术项目(2007AA03Z240)
关键词 RUO2 聚苯胺 涂覆热分解法 电化学聚合 比电容 ruthenium oxide polyaniline coating thermal decomposition electrochemistry polymerization specific capacitance
  • 相关文献

参考文献16

  • 1甘卫平,马贺然,李祥.超级电容器用(RuO_2/Co_3O_4)·nH_2O复合薄膜电极的制备及其性能[J].无机材料学报,2011,26(8):823-828. 被引量:9
  • 2Yoon Y S, Cho W I, Lim J H, et al. Solid-state thin-film supercapacitor with ruthenium oxide and solid electrolyte thin films [J]. Power Sources, 2001, 101(1): 126-129.
  • 3Kim H, Popov B N. A mathematical model of oxide/carbon composite electrode for super-capacitors [J]. Journal of the Electrochemical Society, 2003, 150(9): Al153-Al160.
  • 4李祥,甘卫平,马贺然,刘泓.胶体法制备60%RuO_2-AC复合电极材料及其性能[J].复合材料学报,2011,28(3):90-95. 被引量:2
  • 5Zheng J P, Jow T R. A new charge storage mechanism for electrochemical capacitors [J]. Journal of the Electrochemical Society, 1995, 142(1)- L6-L7.
  • 6Park J H, Park O O. Hybrid electro- chemical capacitors based on polyaniline and aetivatedcarbon electrodes [J]. Journal of Power Sources, 2002, 111(1) : 185-190.
  • 7Fusalba F, Meholi N E, Breau L, et al. Physico-chemical and electrochemical charaeterization of polycyclopenta [2,1- b ; 3,4 -hi dithio- phen- 4- one as an active electrode for electro chemical supercapacitor [J]. Chemistry of Materials, 1999, 11 (10) : 2743-2753.
  • 8Conway B E. Electrochemical supercapacitors [M ]. New York: Kluwer Acadmic Publishers/Plenum Press, 1999.
  • 9Wessling B. Scientific and commercial breakthrough for organic metals [J]. Synthetic Metals, 1997, 85(1): 1313-1318.
  • 10Cruz S R, Romero G J, Angulo S J L, et al. Comparative study of polyaniline cast films prepared from enzymatically and chemically synthesized polyaniline [J].Polymer, 2004, 45 (14) : 4711-4717.

二级参考文献20

  • 1苏岳锋,吴锋,包丽颖,杨朝晖.炭钌复合电极碱性电化学电容器的研究(英文)[J].新型炭材料,2007,22(1):53-58. 被引量:6
  • 2Zheng J P, Cygan P J, Jow T R. Hydrous ruthenium oxide as an electrode material for electrochemical capacitors [J]. J Electrochem Soc, 1995, 142(8):2699-2703.
  • 3Nim H, Branko N P. Characterization of hydrous ruthenium oxide/carbon nanocomposite supercapaeitors prepared by a colloidal method [J]. Journal of Power Sources, 2002, 104, 52-61.
  • 4Li H F, Wang R D, Cao R. Physical and electrochemical characterization of hydrous ruthenium oxide/ordered mesoporous carbon composites as supercapacitor [ J ]. Microporous and Mesoporous Materials, 2008, 111: 32-38.
  • 5Lee Y H, OhJ G, Oh H S, et al. Novel method for the preparation of carbon supported nano-sized amorphous ruthenium oxides for supercapacitors [ J]. Electrochemistry Communications, 2008, 10: 1035-1037.
  • 6Zaher Algharaibeh, Liu X R, Peter G. An asymmetricanthraquinone- modified carbon/ruthenium oxide supercapaeitor [J]. Journal of Power Sources, 2009, 187: 640-643.
  • 7Pico F, Morales E, Fernandez J A, et al. Ruthenium oxide/ carbon composites with micropororous of mesoporous carbon as support and prepared by two procedures: A comparative study as supercapacitor electrodes [J]. Electrochimica Aeta, 2009, 54: 2239-2245.
  • 8Chen W C, Hu C C, Wang C C, et al. Electrochemical characterization of activated carbon- ruthenium oxide nanoparticles composites for supercapacitors[J]. Journal of Power Sources, 2004, 125: 292-298.
  • 9Vix-Guterl C, Saadallah S, Jurewicz K. Supercapacitor electrodes from new ordered porous carbonmaterials obtained by a templating procedure. Materials Science and Engineering B, 2004, 108(1/2): 148-155.
  • 10Zheng J P, Xin Y. Characterization of RuO2-xH2O with various water contents. Journal of Power Sources, 2002, 110(1): 86-90.

共引文献9

同被引文献48

引证文献5

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部