摘要
A novel aluminum bronze over the Cu-Al binary alloy eutectoid Cu-14Al-4.5Fe was prepared by a jointly-charging one-melting technique and conventional sand casting. The bronze coatings were atmospherically plasma sprayed on the 45# medium carbon steel substrate. The effect of rare earth Ce on the microstructures and Vickers hardness of the cast alloy and coatings were characterized by scanning electron microscopy, X-ray diffraction, electronic probe microanalysis, transmission electron microscopy and microhardness measurements. The results indicate that the hardness of both as-cast alloy and coating are enhanced by the addition of 0.6% Ce due to the refinement of κ phases which are well distributed in the matrix. The rapid solidification in the plasma spray processing retains Fe-supersaturated in the Al-bronze alloy coatings, which avoids the formation of eutectoid （α＋γ2） phase and stacking faults are found in the coatings with Ce added, accordingly improves the mechanical properties.
采用一次共装熔炼、砂型铸造Al含量超过Cu-Al二元合金共析点的新型铝青铜合金Cu-14Al-4.5Fe,在45#中碳钢表面制备铝青铜等离子喷涂层。通过扫面电镜、X射线衍射分析、电子探针、透射电镜和显微硬度计分析Ce元素对新型铝青铜合金及喷涂层表面组织形貌和维氏硬度的影响。结果表明:添加0.6%Ce到铸态合金及喷涂层可以使细化的κ相均匀分布于基体,并提高材料硬度。等离子喷涂层快速凝固,保留铝青铜涂层中Fe元素的过饱和固溶体,避免生成(α+γ2)共析相。含Ce喷涂层中的堆垛层错是提高材料力学性能的因素。
基金
Projects (50804019, 51165021) supported by the National Natural Science Foundation of China
Project (0901ZTB009) supported by the Super Tutor Foundation from the Education Department of Gansu Province, China