固溶时效工艺对ZA27合金组织和性能的影响 被引量:1

Effect of solution and aging technology on microstructure and properties of ZA27 alloy
原文传递
导出
摘要 采用扫描电镜(SEM)、X射线衍射(XRD)和力学性能测试等手段研究了固溶处理对ZA27合金组织和性能的影响。在300~380℃范围,合金经不同温度固溶处理1 h,水淬后进行相同的时效(160℃×8 h)处理。分析了在不同温度固溶处理的淬火态和时效态合金的显微组织及力学性能。结果表明,在365℃固溶处理能够使溶质原子充分溶入基体,时效析出相数量多、尺寸小、分布均匀,时效强化效果最好。ZA27合金的优选固溶工艺为365℃×1 h。 Effect of solution treatment on microstructure and mechanical properties of ZA27 alloy were studied by means of scanning electron microscopy(SEM),X-ray diffraction(XRD) and mechanical property testing.After solution treatment in the temperature range of 300-380 ℃ for 1 h,the alloy samples were aged at 160 ℃ for 8 h.The results show that complete dissolution of the solute atoms in the ZA27 alloy is obtained after solution treatment at 365 ℃ and uniformly distributed fine precipitates are observed after aging treatment.The proper solution treatment parameters of the alloy are heating at 365 ℃ for 1 h.
出处 《材料热处理学报》 EI CAS CSCD 北大核心 2012年第11期73-77,共5页 Transactions of Materials and Heat Treatment
基金 湖南有色研究基金(2011-01-002)
关键词 ZA27合金 固溶温度 组织 性能 析出相 ZA27 alloy solution temperature microstructure mechanical property precipitate
  • 相关文献

参考文献13

二级参考文献52

共引文献86

同被引文献3

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部