摘要
研究了水性环氧树脂乳液改性水泥砂浆的力学性能、粘结性能、收缩性能和耐久性能，用SEM和MIP分析了砂浆的结构。结果表明，掺加6％～10％水性环氧树脂乳液可有效提高水泥基修补砂浆的力学性能和与老砂浆的粘结强度，降低水泥砂浆的收缩值；水泥砂浆的抗渗性、抗碳化性以及抗冻性能均随水性环氧树脂掺量的增加而显著提高；较之未经改性的普通砂浆，水性环氧树脂乳液改性水泥砂浆的结构更为致密，连通孔的孔隙率和平均孔径小。
The mechanical and adhesive properties,shrinkage and durability of cement mortar modified with water borne epoxy emulsion were experimentally studied,and the mierostructures of the mortars were analyzed by SEM and MIP. The results showed that, adding 6%-10% （solid content） epoxy emulsion based on the mass of the cement in mortar will remarkably improve the me- chanical properties of the mortar, and the adhesive strength of the mortar with aged cement mortar. The drying shrinkage of the modified mortar decreased,and the chloride permeability,carbonation and frost resistance increased with the increase of the polymer amount added. Compared with ordinary cement mortar,the polymer modified cement mortar is more compacted in structure,lower in porosity and small in mean pore size.
出处
《新型建筑材料》
2012年第12期40-42,46,共4页
New Building Materials
基金
浙江省建设科技补助资金项目(200502)
关键词
环氧树脂乳液
水泥砂浆
力学性能
粘结强度
收缩
耐久性
显微结构
epoxy emulsion
cement mortar
mechanical property
adhesive strength
shrinkage
durability
microstructure