不同基底材料与饰面瓷结合界面观察及元素分析

Experimental study of the bonding interface between different base material and veneering porcelain
原文传递
导出
摘要 目的定性分析不同基底材料与饰面瓷之间化学结合的方式。方法本研究于2011年3—9月在大连市口腔医院和大连交通大学完成。以上颌侧切牙为模型,选用镍铬(Ni-Cr)合金、氧化锆、金钯(Au-Pd)合金、压铸瓷、钴铬(Co-Cr)合金、混合Au-Pd合金6种基底材料,按照厂家的操作要求在不同基底材料上烧结饰面瓷。然后用扫描电镜观察各基底材料与饰面瓷界面,并用能谱分析仪进行元素分析。结果 Ni-Cr合金、氧化锆、Au-Pd合金、Co-Cr合金、混合Au-Pd合金5种基底与饰面瓷之间均发生了程度不同的元素扩散,扩散范围约1~2μm。随着远离界面,扩散元素含量逐渐降低直至消失。压铸瓷基底在实验条件下未明显观察到饰面瓷与压铸瓷的结合界面。结论 Ni-Cr合金、氧化锆、Au-Pd合金、Co-Cr合金、混合Au-Pd合金及压铸瓷基底在和饰面瓷的烧结过程中均发生了化学结合。 Objective To observe the changes of chemical elements between the different base material and the veneer- ing porcelain with the electron probe, and analyze the pattern of chemical combination of the different base material and the veneering porcelain. Methods Using the maxillary lateral incisor as a model, Ni-Cr alloy, zirconia, the Au-Pd al- loy, press casting ceramic, Co-Cr alloy and mixed Au-Pd alloy base crown were selected and fired opaque and body por- celain respectively according to the recommended procedures by manufacturere. The thickness of ceramic layer was con- trolled with in 2mm on the labial side. The experimental sample was cut with the low speed diamond saw. Grind, polish and ultrasonically clean the cut surface. The zirconia sample and press casting porcelain sample were sprayed with gold in vacuum. Then observe the interface with electron microscopy, and analyze the situation of the elements exchange and transfer with the line scan and point scan of electron probe in the interracial depth of about 10 μm. Results Element diffusions appeared between the Ni-Cr alloy, zirconia, the Au-Pd alloy, Co-Cr alloy, mixed Au-Pd alloy base crown and veneering porcelain. Some elements could penetrate into veneering porcelain in the range of 1-2 μm, and the extent of el- ement diffusion weakened until it disappeared with the increase of depth. The interface of press casting porcelain crown and veneering porcelain was not found. Conclusion The composition between press casting crown and veneering porce- lain is homogeneity. There is chemical combination between the 5 kind of base crown and the veneering porcelain during the process of firing.
出处 《中国实用口腔科杂志》 CAS 2012年第11期682-685,共4页 Chinese Journal of Practical Stomatology
基金 辽宁省自然科学基金项目(20072149)
关键词 陶瓷 基底-瓷界面 基底材料 元素扩散 ceramic base-porcelain interface base crown element diffusion
  • 相关文献

参考文献10

  • 1金磊,王忠义,李旬科,沈丽娟,张寿华.金沉积烤瓷冠金瓷界面的研究[J].实用口腔医学杂志,2004,20(1):76-79. 被引量:15
  • 2Craig RG, Ward ML. Restorative dental materials [M]. 10th ed. St.Louis : Mosby-Year Book, Inc, 1997 : 484-499.
  • 3Wataha JC. Alloys for prosthodontie restorations [J]. J Prosthet Dent, 2002,87 : 351-63.
  • 4姚汀武.口腔技工工艺学[M].北京:北京科学技术出版,2006:451-453.
  • 5Bowers JE, Vermilyea SG, Gris world WH. Effect of metal conditioners on porcelain-alloy bond strength [J]. J Prosthet Dent, 1985,54 (2): 201-203.
  • 6Fereidoun D, Terry D. Effect of electro-deposition of gold on porcelain-to-metal bond strength [J]. J Prosthet Dent, 1987, 57 ( 1 ): 41-46.
  • 7Smith TB, Kelly JR, Tesk JA. In vitro fracture behavior of ceramic and metal-ceramic restorations [J]. J Prusthodont, 1994,3 ( 3 ): 138-144.
  • 8Kwon JE, Lee SH, Lira HN, et al. Bonding characteristics between zirconia core and veneering porcelain [J]. Dent Mater, 2009,25 : e5-e46/e42.
  • 9殷家悦,张忠提,艾红军,司文捷,包扬.钇稳定氧化锆基底材料与饰面瓷结合性能的实验研究[J].华西口腔医学杂志,2009,27(6):669-672. 被引量:16
  • 10Moustafa NA, Cornelis JK, Albert JF. Microtensile bond strength of different components of core veneered all-ceramic restorations.Part Ⅱ.Zireonnia veneering ceramics [J]. Dent Maer, 2006,22(9) : 857-863.

二级参考文献11

  • 1何帅,陈吉华,王光耀,王少海,沈丽娟,王辉.不同表面处理方法对氧化锆支架材料与Vitadur alpha瓷结合性能的影响[J].上海口腔医学,2005,14(4):397-401. 被引量:11
  • 2Tinschert J, Schulze KA, Natt G, et al. Clinical behavior of zirconia-based fixed partial dentures made of DC-Zirkon: 3-year results[J]. Int J Prosthodont, 2008, 21 (3):217-222.
  • 3Sailer I, Feher A, Filser F, et al. Prospective clinical study of zirconia posterior fixed partial dentures: 3-year follow-up[J]. Quintessence Int, 2006, 37 (9) : 685-693.
  • 4Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Mierotensile bond strength of different components of core veneered all-ceramic restorations. Part Ⅱ: Zirconia veneering ceramics[J]. Dent Mater,2006, 22 (9) : 857-863.
  • 5Fischer J, Stawarczyk B. Compatibility of machined Ce-TZP/Al2O3 nanocomposite and a veneering ceramic[J]. Dent Mater, 2007, 23 (12) : 1500-1505.
  • 6Coffey JP, Anusavice K J, DeHoff PH, et al. Influence of contraction mismatch and cooling rate on flexural failure of PFM systems[J]. J Dent Res, 1988, 67(1):61-65.
  • 7Guess PC, Kulis A, Witkowski S, et al. Shear bond strengths between different zirconia cores and veneering ceramics and their susceptibility to thermocycling [J]. Dent Mater, 2008, 24 (11) : 1556-1567.
  • 8Anusavice KJ, Dehoff PH, Fairhurst CW. Comparative evaluation of ceramic-metal bond tests using finite element stress analysis [J]. J Dent Res, 1980, 59 (3) : 608-613.
  • 9Ashkanani HM, Raigrodski AJ, Flinn BD, et al. Flexural and shear strengths of ZrO2 and a high-noble alloy bonded to their corresponding porcelains[J]. J Prosthet Dent, 2008, 100(4):274- 284.
  • 10吕宏,KerschbaumT.H,FaberF.J,冯海兰.金沉积烤瓷全冠[J].中华口腔医学杂志,2000,35(5):395-397. 被引量:51

共引文献29

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部