新型中锰马氏体高强度钢的耐磨性能 被引量:10

Wear Resistant of New Type Medium Manganese High Strength Martensite Steel
原文传递
导出
摘要 利用销盘式磨料磨损试验和三体冲击磨料磨损试验研究碳质量分数分别为0.12%和0.19%新型中锰马氏体高强度钢的磨损行为,并与Hardox450钢和21C钢进行耐磨性能对比。用磨损失重量表征耐磨性能,利用LOM、SEM和XRD等设备研究材料磨料磨损机制。结果表明,新型中锰钢耐磨性能与Hardox450钢及21C钢相当。在销盘式磨料磨损试验和三体冲击磨料磨损试验中,马氏体高强钢的耐磨性能与材料的硬度呈线性关系,硬度越高,材料耐磨性越好。由于锰的添加,新型中锰钢的优点不仅在于具有锰的固溶强化特性提高耐磨性能,还在于该钢的淬透性几乎与该钢的冷却速度无关,因而该钢具有大规模工业生产的潜力。 The abrasive wear behavior of new type medium manganese high strength martensite steels with 0.12% and 0.19% carbon content were determined by the pin-on-disc abrasion test and three-body impact abrasive test,and was contrasted with steels of Hardox450 and 21C.The wear properties of the specimens were evaluated by weight loss measurements.In order to evaluate the wear mechanism of different steels,the post-test characterization of the worn surfaces were performed using LOM,SEM and XRD.The results show that the wear resistance of new type medium manganese martensite steels is comparable with the wear resistant steels of Hardox450 and 21C.The wear weight lost of the studied steel tested both in pin-on-disc abrasion and three-body impact abrasion is approximately linearly proportional to its HV hardness,i.e.,the higher the hardness,the better wear resistance of steels.Due to the addition of medium-Mn,the new typed steel assumes the advantages not only the Mn-solid strengthening to improve the wear resistance ability but its hardenability could be obtained at all cooling rate,which make the steel has the potential to be produced in steel industry.
出处 《钢铁》 CAS CSCD 北大核心 2012年第12期64-70,共7页 Iron and Steel
基金 国家973计划资助项目(2010CB630803)
关键词 耐磨钢 马氏体 高强度 磨料磨损 wear resistance steel martensite high strength abrasive wear
  • 相关文献

参考文献17

  • 1Dastur Y N,Leslie W C. Mechanism of Work Hardening in Hadfield Manganese Steel [J]. Metallurgical and Materials Transactions A, 1981,12 (5) : 749.
  • 2Yan W L,Fang L,Sun K,et al. Effect of Surface Work Hard- ening on Wear Behavior of Hadfield Steel[J]. Mater Sci Eng A,2007(460-461) :542.
  • 3王存宇,时捷,刘苏,杜劭峰,董瀚.淬火-配分-回火工艺处理钢的三体冲击磨损性能研究[J].材料研究学报,2009,23(3):305-310. 被引量:11
  • 4曹艺,王昭东,吴迪,张逖.NM400高强度低合金耐磨钢的组织与性能[J].东北大学学报(自然科学版),2011,32(2):241-244. 被引量:23
  • 5王昭东,邓想涛,曹艺,王国栋,顾林豪,宋增强.新型低成本超高强低合金耐磨钢研究及其工业化应用[J].钢铁,2010,45(8):61-64. 被引量:28
  • 6Jose Renden M O. Abrasive Wear Resistance of Some Com- mercial Abrasion Resistant Steels Evaluated by I,aboratoryTest MethodsEJ]. Wear,2009,267(11) :2055.
  • 7Sundstrom A,Rendon J,Olsson M. Wear Behaviour of Some Low Alloyed Steels Under Combined Impact/Abrasion Con- tact Conditions[J] Wear,2001,250(1-12) :744.
  • 8中华人民共和国国家质量监督检验检疫总局,中国国家标准化管理委员会.GB/T24186-2009工程机械用高强度耐磨钢板[S].北京:中国标准出版社,2010.
  • 9刘军刚,冯璟,蔡晓娟,韩笑.耐磨钢生产现状与分析[J].莱钢科技,2010(2):1-3. 被引量:4
  • 10SHI Jie, CAO Wen-quan. Ultrafine Grained High Strength Low Alloy Steel With High Strength And High Ductility[J]. Materials Science Forum, 2010,654-656 : 238.

二级参考文献26

共引文献236

同被引文献77

引证文献10

二级引证文献37

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部