NaYF_4∶Yb^(3+),Tm^(3+)负载壳聚糖微球的制备及发光性质研究 被引量:1

Fabrication and Luminescent Property of NaYF_4∶Yb^(3+),Tm^(3+) Loaded Chitosan Microspheres
下载PDF
导出
摘要 采用溶剂热法合成了聚乙烯亚胺(PEI)修饰的NaYF4∶Yb3+,Tm3+纳米晶。产物具有良好的结晶性,粒径分布均匀,可稳定分散在水溶液中。通过微乳法制备了NaYF4∶Yb3+,Tm3+纳米晶负载壳聚糖微球。结果表明:纳米晶均匀地嵌在壳聚糖微球的表面壳层,球核为纯壳聚糖的交联产物。粗糙的球体表面使微球具有较好的分散性。在980 nm近红外光激发下,纳米晶负载壳聚糖微球具有良好的上转换发光特性,发光强度随纳米晶负载量的增加而增大,通过调控纳米晶的负载量可实现对纳米晶负载壳聚糖微球发光强度的调控。 Upconversion nanocrystals have caused much attention,due to their superior optical and chemical properties.In this study,upconversion nanocrystals loaded chitosan microshperes were designed to develop the applications in biomedicine.Polyethyleneimine(PEI) modified NaYF4∶Yb3+,Tm3+ upconversion nanocrystals were prepared by solvothermal method.XRD and TEM indicated that the particles crystallized very well and the size was about 20 nm.The dispersity was enhanced,both in water and in chitosan solution.NaYF4∶Yb3+,Tm3+ loaded chitosan microshperes were fabricated using microemulsion method.SEM pictures showed that the chitosan microspheres' surface was rough and the NaYF4∶Yb3+,Tm3+ particles were embedded in the surface shell.For PEI and chitosan having the same positive charge,during the cross-linking process,PEI modified particles moved to the surface of the chitosan microshperes drived by repulsive force.The luminescence intensity of the NaYF4∶Yb3+,Tm3+ loaded chitosan microshperes increased with the increasing of nanopaticles.Due to the biocompatibility and biodegradability of the chitosan carrier,this material can improve the duration in vivo,avoid process release effect.This kind of nanocrystals loaded chitosan microshperes may have broad application prospects in photodynamic therapy,biological imaging,fluorescent identification,as controlled release materials.
出处 《发光学报》 EI CAS CSCD 北大核心 2013年第2期160-164,共5页 Chinese Journal of Luminescence
基金 海南省国际科技合作重点项目计划(GJXM201103)资助项目
关键词 溶剂热法 上转换发光 壳聚糖微球 solvothermal synthesis upconversion fluorescence chitosan microshpere
  • 相关文献

参考文献21

  • 1芦志华,陈欢,何春凤,揣晓红,秦冠仕,赵丹.聚乙烯吡咯烷酮修饰的NaYF_4∶Yb^(3+)/Er^(3+)上转换发光纳米粒子的制备及其生物兼容性[J].发光学报,2011,32(10):993-997. 被引量:4
  • 2Sandrock T,Scheife H,Heumann E. High-power continuous-wave upconversion fiber laser at room temperature[J].Optics Letters,1997,(11):808-810.
  • 3Downing E,Hesselink L,Ralston J. A three-color,solid-sate,three-dimensional display[J].Science,1996,(5279):1185-1189.
  • 4de Camargo A S S,Possatto J F,Nunes L A O. Infrared to visible frequency upconversion temperature sensor based on Er3+-doped PLZT transparent ceramics[J].Solid State Communications,2006,(1/2):1-5.
  • 5Kr(a)mer K W,Biner D,Frei G. Hexagonal sodium yttrium fluoride based green and blue emitting upconversion phosphors[J].Chemistry of Materials,2004,(07):1244-1251.
  • 6Wang F,Liu X. Upconversion multicolor fine-tuning:Visible to near-infrared emission from lanthanide-doped NaYF4 nanoparticles[J].Journal of the American Chemical Society,2008,(17):5642-5643.doi:10.1021/ja800868a.
  • 7Cheng L,Yang K,Shao M. Multicolor in vivo imaging of upconversion nanoparticles with emissions tuned by luminescence resonance energy transfer[J].Journal of Physical Chemistry C,2011,(06):2686-2692.
  • 8Boyer J C,Manseau M P,Murray J I. Surface modification of upconverting NaYF4 nanoparticles with PEGphosphate ligands for NIR(800 nm)biolabeling within the biological window[J].Langmuir,2010,(02):1157-1164.doi:10.1021/la902260j.
  • 9Hampl J,Hall M,Mufti N A. Upconverting phosphor reporters in immunochromatographic assays[J].Analytical Biochemistry,2001,(02):176-187.
  • 10Chen Z,Chen H,Hu H. Versatile synthesis strategy for carboxylic acid-functionalized upconverting nanophosphors as biological labels[J].Journal of the American Chemical Society,2008,(10):3023-3029.

二级参考文献54

  • 1杨魁胜,李岩,余朝义,卢利平,叶灿华,张希艳.Upconversion Luminescence Properties of Ho^(3+),Tm^(3+),Yb^(3+) Co-Doped Nanocrystal NaYF_4 Synthesized by Hydrothermal Method[J].Journal of Rare Earths,2006,24(6):757-760. 被引量:12
  • 2Auzel F. Upconversion and anti-stokes processes with f and d ions in solids [J]. Chem. Rev. , 2004, 104( 1 ) :139-173.
  • 3Huang L H, Liu X R, Xu W, et al. Infrared and visible luminescence properties of Er^3+ and Yb^3+ ions codoped Ca3Al2Ge3O12 glass under 978 nm diode laser excitation [ J]. J. Appl. Phys. , 2001, 90(11) :5550-5553.
  • 4Man S O, Pun E Y B, Chuang P S. Upconversion luminescence of Er^3+ in alkali bismuth gallate glasses [ J ]. Appl. Phys. Lett. , 2000, 77(4) :483-485.
  • 5Wang F, Dev K Chatterjee, Li Z Q, et al. Synthesis of polyethylenimine/NaYF4 nanoparticles with upconversion fluorescence [J]. 2006, 17(23):5786-5791.
  • 6Shen J, Sun L D, Yan C H. Luminescent rare earth nanomaterials for bioprobe applications [ J ]. Dalton Trans. , 2008, (42) :5687-5697.
  • 7Wang L Y, Li Y D. Green upconversion nanocrystals for DNA detection [ J]. Chem. Commun., 2006, (24): 2557-2559.
  • 8Hu H, Xiong L Q, Zhou J, et al. Multimodal-Luminesence core-shell nanocomposites for targeted imaging of tumor cells [J]. Chem. Eur. J. , 2009, 15(14):3577-3584.
  • 9Qin G S. Rare earth ions doped violet and ultraviolet upconversion laser materials and laser manipulation of a bubble [ D ]. Changchun: Changchun Institute of Optics, Fine Mechanics and Physics, 2004 (in Chinese).
  • 10Wang G F, Qin W P, Wang L L, et al. Intense ultraviolet upconversion luminescence from hexagonal NaYF4: Yb^3+/Tm^3+ microcrystals [J]. Optics Express, 2008, 16(16):11907-11914.

共引文献54

同被引文献2

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部