采用化学镀方法在碳钢上沉积非晶Ni-P合金镀层(10.90wt.%),考察Ni-P合金结构、性能及热处理温度对耐蚀性的影响。结果表明:在10%HCl溶液中,非晶Ni-P镀层具有较好的耐蚀性;热处理影响镀层的耐蚀性,非晶Ni-P镀层经200℃热处理后,可使耐蚀性能提高37%,热处理温度达到300℃和400℃时,镀层分别出现亚稳相和稳定相,耐蚀性能降低,但耐蚀性仍优于镀态Ni-P镀层。
The amorphous Ni-P coatings （10.90 wt. % ） were deposited on carbon steel by electroless method, furthermore, the effect of as-deposits structure, properties and heattreatment temperture on the corrsion resistance were investigated. The results show that the corrsion resistance of amorphous Ni-P coatings is superior in 10% HCl soultion. The corrsion resistance is affected by heat treatment, as the performance of corrsion resistance has improved 37% after amorphous Ni-P coatings heated at 200℃. Additionally, metastable and stable phases are presented in Ni-P coatings as the temperature reaches at 300 and 400℃ respectively, however, the corrsion resistance is reduced, which is still higher than as-deposited Ni-P coatings.
出处
《沈阳理工大学学报》
CAS
2013年第1期11-13,36,共4页
Journal of Shenyang Ligong University
关键词
化学镀
Ni—P合金
非晶
热处理
耐蚀性
electroless
Ni-P alloy
amorphous
heat treatment
corrsion resistance