固溶时效处理对触变成形AZ91D镁合金组织和性能的影响研究 被引量:2

Effects of Solution Aging Treatment on Microstructure and Properties of Thixoformed AZ91D Magnesium Alloy
原文传递
导出
摘要 研究了固溶时效处理对触变成形AZ91D镁合金组织演变的影响以及合金组织与力学性能之间的关系。结果表明:固溶时效处理对AZ91D镁合金的显微组织有明显的影响,时效一定时间后析出相连成片状分布于晶界;合金具有明显的时效硬化特征,经固溶时效处理16h后合金的抗拉强度为210 MPa,屈服强度为147 MPa,硬度为HV66,分别比铸态时的提高了98MPa、65MPa和HV10;铸态合金的拉伸断口为沿晶断裂,而固溶时效处理后合金呈现沿晶断裂和解理断裂混合型断口,且解理断裂特征明显。 The effects of solution and aging on microstructure evolution of thixoformed AZglD magnesium alloy were studied as well as relation between alloy microstructure and mechanical properties. The results show that solution and aging treatment have a significant impact on microstructure of the alloy. The pre-cipitated phase is distributed at the grain boundaries in the form of flake after a certain time of aging. The alloy has obvious age-hardening characteristics. After solution and aging for 16 h, tensile strength, yield strength and hardness of the alloy are 210 MPa, 147 MPa and HV66,respectively, 98 MPa, 65 MPa and HV10 higher than those of the cast alloy. The cast alloy presents intergranular fracture,transformed into intergranular-cleavage mixed fracture of obvious cleavage fracture characteristics after solution and aging.
出处 《稀有金属与硬质合金》 CAS CSCD 北大核心 2013年第2期37-40,共4页 Rare Metals and Cemented Carbides
基金 四川省教育厅重点项目(12ZA202)
关键词 镁合金 触变成形 固溶时效 显微组织 力学性能 拉伸断口 magnesium alloy thixoforming solution and aging microstructure mechanical properties tensilefracture
  • 相关文献

参考文献7

二级参考文献22

  • 1布鲁克斯C R 丁夫(译).有色金属的热处理组织与性能[M].北京:冶金工业出版社,1988..
  • 2Alan Luo, Jean Renaud, Isao Nakatsugawa, et al. Magnesium castings for automotive applications[J]. JOM, 1995, 47(7): 28 ~ 31.
  • 3Froes F H, Eliezer D, Aghion E. The science, technology, and applications of magnesium[J]. JOM, 1998, 50(9): 30 ~ 34.
  • 4Song G L, Atrens A,St John D. An hydrogen evolution method for the estimation of the corrosion rate of magnesium alloys[A]. Magnesium Technology 2001[M] ,Edited by J Hryn, TMS (The Minerals, Metals & Materials Society), 2001, 255.
  • 5中国机械工程学会热处理专业学会<热处理手册>编委会.热处理手册[M].第二版.北京:机械工业出版社,1991,482.
  • 6B.C.柯瓦连科.金相试剂手册[M].北京:冶金工业出版社,1973,90.
  • 7Lunder O, Lein J E, Aune T Kr, Nisancioglu K. The role of Mg17Al12 phase in the corrosion of Mg alloy AZ91[J]. Corrosion, 1989, 45(9): 741 ~ 748.
  • 8Song G L, Atrens A, STJohn D, et al. The anodic dissolution of Magnesium in chloride and sulphate solutions[J]. Corrosion Science, 1997, 39( 10 -11): 1981~2004.
  • 9顾根富,高伟,张修智,顾伟,叶平.微量钇稀土合金化对高强铝合金LY12CZ焊接热裂纹倾向性的影响[J]金属科学与工艺,1987(01).
  • 10胡连喜,杨绮雯,罗守靖,徐欣颖.铝/氧化铝纤维预制体的液态浸渗动力学[J].中国有色金属学报,1998,8(A01):75-79. 被引量:10

共引文献169

同被引文献22

引证文献2

二级引证文献16

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部