自孕育工艺参数对ZA96镁合金半固态组织的影响及其交互本质 被引量:8

Effects of self-inoculation technological parameters on semi-solid microstructure of ZA96 magnesium alloy and interactive nature
下载PDF
导出
摘要 采用自孕育法制备ZA96镁合金半固态组织,研究自孕育工艺参数对ZA96镁合金半固态组织的影响,并从温度场的角度分析工艺参数之间相互作用的本质。结果表明:采用白孕育法铸造,能够获得合格的半固态坯料和浆料。工艺参数对半固态坯料组织影响较大,但对从导流器出口处收集到的浆料在半固态区间进行保温后,发现自孕育剂加入量对组织影响不大,而导流器角度的影响较大。熔体过热度为80-95℃、自孕育剂加入量为5%、导流器角度为45。时,半固态坯料组织的晶粒平均尺寸较小,约为35.6μm;或经552℃、20s保温后,其晶粒尺寸为45μm,圆整度为1.7。自孕育工艺参数交互作用的本质在于通过白孕育参数的调整从而达到控制其形核的目的。推导出了熔体在导流器出口处的温度与自孕育工艺参数之间的关系式。 Abstract: Semi-solid microstructure of ZA96 magnesium alloy was prepared by self-inoculation method (SIM). The effects of self-inoculation technological parameters on the microstructure of semi-solid ZA96 magnesium alloy were investigated. And the nature of interactive effect between technological parameters was analyzed from the standpoint of temperature field. The results show that high-quality semi-solid billets and slurry can be obtained by SIM. The effects of self-inoculation technological parameters on the microstructure of semi-solid billets are bigger, but for the microstructure of semi-solid slurry which is collected from the exit of the fluid director and holding in semi-solid interval, the effect of self-inoculants is smaller, but that of the angle of fluid director is bigger. When the superheat of the melt is 80-95 ℃ and the addition of self-inoculants is 5% and the angle of fluid director is 45°, the grain size of semi-solid billet is 35.6 μm; or after holding 20 s at 552 ℃, the grain size of primary phase is 45μm and the roundness is 1.7. The interactive nature of self-inoculation technology parameters is to control nucleation by coordinating them. The formula between the temperature of melt in the exit of fluid director and self-inoculation technological parameters was derived.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2013年第3期599-609,共11页 The Chinese Journal of Nonferrous Metals
基金 国家重点基础研究发展计划前期预研项目(2010CB635106) 国家自然科学基金资助项目(50964010)
关键词 ZA96镁合金 半固态组织 工艺参数 自孕育法 交互本质 ZA96 magnesium alloy semi-solid microstructure technological parameter self-inoculation method interactive nature
  • 相关文献

参考文献19

  • 1LUO A A. Magnesium: current and potential automotive application[J]. JOM, 2002, 54: 42-48.
  • 2FLEMINGS M C. Behavior of metals and alloys in the semi-solid state[J]. Metall Trans A, 1991, 22:957-981.
  • 3PAN Q Y, FINDON M, APELIAN D. The continuous rheoconversion process (CRP): A novel SSM approach[C]// Proceedings of the 8th International Conference on Semi-Solid Processing of Alloys and Composites. Limassol: North American Die Casting Association, 2004.
  • 4YURKO J A, MARTINEZ R A, FLEMINGS M C. Development of semisolid rheocasting (SSR)[C]// Proceeding of the 7th International Conference on Semi-Solid Processing of Alloy and Composites. Tsukuba, Japan: National Institute of Advanced Industrial Science and Technology, 2002: 659-664.
  • 5GUO H M, YANG X J. Efficient refinement of spherical grain by LSPSF rheocasting process[J]. Materials Science and Technology, 2008, 24(1): 55 63.
  • 6路贵民,董杰,崔建忠,常守威.7075 Al合金液相线半连续铸造组织及形成机理[J].金属学报,2001,37(10):1045-1048. 被引量:32
  • 7KAUFMANN H, MUNDI A, POTZINGER R, UGGOWITZER P J, ISHIBASHI N. An update on the new rheo-casting- development work for Al-and Mg-alloys[J]. Die Casting Engineer, 2002(4): 16-19.
  • 8XING Bo, LI Yuan-dong, MA Ying, CHEN Ti-jun, HAO Yuan. Microstructure of partially remelted billet of AM60 alloy prepared with self-inoculation method[J]. Transactions of Nonferrous Metals Society of China, 2010, 20:1622-1629.
  • 9曲俊峰,李元东,邢博,张鹏.自孕育法流变压铸AZ91D镁合金微观组织特征[J].铸造,2010,59(5):454-458. 被引量:7
  • 10严楷,李元东,马颖,陈体军.熔体处理温度对自孕育法制备AZ61半固态浆料的影响[J].特种铸造及有色合金,2011,31(5):424-427. 被引量:2

二级参考文献75

共引文献325

同被引文献83

  • 1郭洪民,杨湘杰,胡斌.转动输送管制浆工艺参数对A356合金半固态组织的影响[J].中国有色金属学报,2004,14(12):2049-2054. 被引量:46
  • 2管仁国,康立文,尚剑洪,王超,温景林.倾斜式冷却剪切工艺条件对半固态合金组织的影响[J].特种铸造及有色合金,2005,25(10):600-603. 被引量:22
  • 3王立娟,张万金,吴欣凤.变形铝合金熔炼与铸造[M].长沙:中南大学出版社,2010.
  • 4M.C.Flem ings.Behavior of Metal Alloys in the Semi -solid State.Metall.Trans.,1991,22k (4) :957-981.
  • 5H. Kaufmann, A. Mundi, R.Potzinger,P.J.Uggowitzer,N.Ishibashi.Anupdate on the new rheo-casting development work for Al-and Mg-alloys[J].Die Casting Engineer,2002(4 ): 16-19.
  • 6Z.Fan.Development of the rheo -diecasting process for magnesiumalloys[J].Mater.Sci.Eng.A,2005 (413-414) :72-78.
  • 7J.A.Yurko,R.A.Martinez, M. C. Flemings. Development of semisolidrheocasting (SSR). In:Y. Tsutsui, M. Kiuchi and K.Ichikawa, eds.Proceedings of the 7th International Conference on Semi -solidprocessing of Alloys and CompositesJapan:National Institute ofAdvanced Industrial Science and Technology Japan Society forTechnology of Plasticity, 2002 : 659-664.
  • 8D.Doutre,G.Hay,P.Wales.SEED:A new process for semi-solid form-ing.Canadian Metallurgical and process overview.Solid StatePhenomena, 2006( 116-117):472-477.
  • 9Stefanescu D M,Kanetkar C S.State of the art of counter simulationof casting and solidification process [M].Paris:Les Edition dephysiqne,1986.
  • 10Nafisi S,Ghomashchi M R.The Microstructure Characterization ofSemi-solid Slurries[J]JOM.2006,6:24-30.

引证文献8

二级引证文献30

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部