三层复合PI薄膜厚度比对其电导特性影响 被引量:4

The Influence of Thickness Ratio of Three-layer PI Composite Films on Conductance Property
下载PDF
导出
摘要 以微乳化-热液法制备硅/铝氧化物纳米分散液,并制备了一系列掺杂层与中间层厚度比不同的纳米掺杂三层复合聚酰亚胺(PI)薄膜.在相同环境条件下进行了薄膜的透射电镜(TEM)测试和电导电流测试.TEM测试结果可以直接观察到纳米粒子在有机基体中分散均匀,且可得到三层复合薄膜的复合结构,掺杂层和中间层的尺寸比例符合实验要求.复合薄膜的电导电流在同一电场强度下随着掺杂层厚度比例的增加逐渐增大,而电老化阈值随着掺杂层厚度比例增大向低场强方向移动. Micro emulsion-hydrothermal method was used in preparing a series of three-layer PI composite films, which have different thickness ratio of doped PI layer and pure PI layer. Their mierostructure and conduction current were tested by TEM and electrical current experiment devices under the same conditions. Composite films could clearly show from TEM test, the dimension scale of doped PI layer and pure PI layer was fit with experimental requirements, and nano-particles dispersed well in organic matrix. Under the same electric field strength, the conduction current of composite films were increased with doped layer thickness increasing. Electrical degradation threshold showed a decreasing trend when doped layer thickness increased.
出处 《哈尔滨理工大学学报》 CAS 2013年第2期21-24,29,共5页 Journal of Harbin University of Science and Technology
基金 国家自然科学基金(50373008)
关键词 聚酰亚胺薄膜 纳米杂化 透射电镜 电导电流 polyimide films nano-composite transmission electron microscope conduction current
  • 相关文献

参考文献19

二级参考文献231

共引文献182

同被引文献71

引证文献4

二级引证文献36

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部