摘要
采用传统的高温熔融法制备了80GeO2–20RO(R=Ca,Sr,Ba)掺铋锗酸盐玻璃。研究了铋掺杂锗酸盐玻璃超宽带近红外发光性质,探讨了铋离子掺杂玻璃超宽带发光机理。结果表明:在808nm激光激发下,铋掺杂锗酸盐玻璃随着碱土金属离子半径增加,中心波长为1300nm的发射强度逐渐降低;在690 nm激光激发下,铋掺杂锗酸盐玻璃的近红外发射覆盖从900 nm到2 000 nm波段但不呈现正态分布,荧光半高宽达428 nm。随着碱土金属离子半径的增加,其近红外发射中心位置逐渐向长波方向移动,推测近红外发光可能源于两种不同形式铋的发光中心。铋掺杂的锗酸盐玻璃具有良好的光学性能,较宽的荧光半高宽,将成为未来超宽带光纤放大器的增益介质。
The Bi-doped germanate glass with the molar composition of 80GeO2-20RO （R = Ca, Sr, Ba） was prepared by a conven- tional melting-quenching technique. The broadband infrared luminescence properties of the glasses were investigated, The infrared luminescence intensity decreases with the increase of the radius of alkaline earth ion under 690 nm and 808 nm excitation, respectively. The excitation at 690nm produces a emission band in the range from 900 to 1 900nm, and the full width at halfa maximum （FWHM） of broad infrared fluorescence reaches up to 428 urn. It is suggested that the infrared emissions could be due to the presence ofBi＋ and BiO. The bismuth-doped germanate glass has a superior optical performance with broad FWHM, which could be used as a gain medium of super broadband fiber amplifier in future.
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2013年第7期1015-1018,共4页
Journal of The Chinese Ceramic Society
基金
国家重点基础研究发展计划"973"项目(2011CB211708)
国家自然科学基金(51002068
51272097
61265004)
云南省应用基础研究青年基金(2012FD009)资助项目
关键词
铋离子掺杂锗酸盐玻璃
红外发光
光学性质
bismuth doped germanate glass
optical properties
infrared luminescence