膜分散微结构反应器制备纳米氧化锌的实验及模型 被引量:2

Preparation of nano-ZnO in membrane dispersion micro-reactor and modeling
下载PDF
导出
摘要 以硫酸锌和氢氧化钠为原料,在膜分散微结构反应器中通过快速均匀混合制备得到颗粒平均尺寸为10~20 nm的氧化锌,并利用混合尺度模型模拟了微反应器内纳米颗粒的成核、生长和团聚过程。模拟计算结果表明,在最初的0.6 ms内颗粒成核占主导地位,在1.6 ms以后以生长为主,同时由于颗粒数密度较大,颗粒运动碰撞造成团聚效应,使得颗粒尺寸具有一定的分布。混合尺度和反应物浓度对颗粒直径和分布有很大影响。模拟结果表明当混合尺度从50 μm减少到5 μm,纳米氧化锌颗粒从19 nm降低到12 nm。微反应器制备实验结果表明,随着膜孔径的减小,混合强度增加,纳米氧化锌颗粒平均直径从20 nm 降低至11 nm,当初始反应物浓度从0.05 mol·L-1提高到0.20 mol·L-1,氧化锌纳米颗粒尺寸由10 nm增大至16 nm。颗粒平均直径及分布的模拟值与实验值相符较好。 Nano-sized ZnO particles were prepared by using zinc sulfate and sodium hydroxide as raw materials in the membrane dispersion micro-structured reactor by rapid mixing precipitation.The mixing scale model was used to simulate the precipitation process of nucleation,growth and agglomeration in the membrane reactor.Modeling results showed that particle nucleation dominated in the initial 0.6 ms,and after 1.6 ms,growth dominated.At the same time,due to a large number of particles,particles collision would cause aggregation,resulting in specific distribution of particle size.Mixing scale and reactant concentration had a great influence on particle diameter and distribution.Simulation results showed that when mixing scale reduced from 50 μm to 5 μm,average diameter of nano-ZnO particles decreased to 12 nm from 19 nm.Experimental results showed that with the decrease of membrane pore size,average diameter of nano-ZnO particles dropped down from 20 nm to 11 nm,and when initial reactant concentration increased from 0.05 mol·L-1 to 0.20 mol·L-1,average diameter of ZnO nanoparticles increased from 10 nm to 16 nm.Simulated average particle diameter and its distribution agreed well with the experimental values.
出处 《化工学报》 EI CAS CSCD 北大核心 2013年第11期4246-4254,共9页 CIESC Journal
基金 国家重点基础研究发展计划项目(2013CB733600) 国家自然科学基金项目(20976096,21276140,21036002) 中国石油科技创新基金研究项目(2011D-5006-0407) 清华大学基础科研项目(20121087993)~~
关键词 膜分散微反应器 纳米氧化锌 混合尺度模型 颗粒分布 membrane dispersion micro-reactor nano-ZnO mixing scale model particle size distribution
  • 相关文献

参考文献6

二级参考文献55

  • 1陈建峰,陈甘棠.混合-反应结晶过程(Ⅱ)模型及验证[J].化工学报,1994,45(2):183-190. 被引量:6
  • 2陆杰.反应结晶(沉淀)研究(学位论文)[M].天津:天津大学,1997..
  • 3[3]
  • 4[4]QI Limin,MAjiming,CHENG Humin,et al.Preparation of BaSO4 nanoparticles in non-ionic w/o microemulsions[J].Colloids and Surfaces A:PhysicochemEngAspects,1996,108:117-126
  • 5陆杰,学位论文,1997年
  • 6Yoshiaki Kawashima, Tomoaki Hino, Hirofumi Takeuchi,Toshiyuki Niwa, Katsuhiko Horibe. Journal of Colloid and Interface Science, 1991, 145(2): 512-523
  • 7Nakashima T, Shimizu M, Kukizaki M. Key Engineering Materials, 1991, 61-62:513-516
  • 8Ryoh Latoh, Yuzoh Asano, Atusi Furuya, Kazuyoshi Sotoyama,Mamoru Tomita. Journal of Membrane Science, 1996, 113:131-135
  • 9Volker Schroder, Olaf Behrend, Helmar Schubert. Journal of Colloid and Interface Science, 1998, 202: 334-340
  • 10ShinzoOmi, Ken'ichi Katami, Arihiro Yamamoto, Marnoru Iso.Journal of Applied Polymer Science, 1994, 51: 1-11

共引文献28

同被引文献27

  • 1胡英顺,尹秋响,侯宝红,王静康.结晶及沉淀过程中粒子聚结与团聚的研究进展[J].化学工业与工程,2005,22(5):371-375. 被引量:15
  • 2Zhang C, Wang Y, Bi S, et al. Preparation of mesoporous ZnO micmspheres through a membrane-dispersion micro- structured reactor and a hydrotherrnal treatment[J]. Ind & gng Chem Res, 2011, 50(23): 13355-13361.
  • 3Chen G G, Luo G S, Yang X R, et al. Preparation of ul tra-fine TiO4 particles using micrcomixing precipitation technology[J]. J Inorg Mater, 2004, 19(5) : 1163-1167.
  • 4Chen G G, Luo G S, Yang L M, et al. Synthesis and size control of CaHPO4 particles in a two-lictuid phase micro-mixing process[J]. J Cryst Growth, 2005, 279 (3) : 501 -507.
  • 5Wang Y, Xu D, Sun H, et al. Preparation of pseudo- boehmite with a large pore volume and a large pore size by using a membrane-dispersion mierostruetured reactor through the reaction of CO2 and a NaA1O2 solution[J]. Ind & Eng Chem Res, 2011, 50(7) : 3889-3894.
  • 6Liu X, Zhang J, Wang L, et al. 3D hierarchically por- ous ZnO structures and their funetionalization by Au nanoparticles for gas sensors[J]. J Mater Chem, 2011, 21(2) :349-356.
  • 7Jing Z, Zhan J. Fabrication and gas-sensing properties of porous ZnO nanoplates[J]. Adv Mater, 2008, 20 (23):4547-4551.
  • 8Qiu Y, Chen W, Yang S. Facile hydrothermal prepara- tion of hierarchically assembled, porous single-crystal- line ZnO nanoplates and their application in dye-sensi- tized solar cells[J]. J Mater Chem, 2010, 20(5): 1001 -1006.
  • 9Tong Y, Cao F, Tang P, et al. Photocatalytic behav- iors of porous ZnO hierarchical structures fabricated via a precursor-pyrolyzing route[J]. J Mater Sci: Ma- ter in Electr, 2013, 24(1) : 89-95.
  • 10Wang W, Tian Y, Wang X, et al. Ethanol sensing properties of porous ZnO spheres via hydrothermal route[J]. J Mater Sci, 2013, 48(8): 3232-3238.

引证文献2

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部