采用硬脂酸法合成纳米晶 Sr Mgx Ti1 - x O3( x=0 .1～ 0 .5)材料 .用 DTA,TG,XRD,IR,XPS和 TEM进行表征 .结果表明 ,粉末粒径 d随 Sr Mgx Ti1 - x O3中镁含量、烧结温度和烧结时间的改变而变化 ;烧结所产生的粉末粒度分布均匀、大小适中 ;Mg2 + 部分替代 Sr Ti O3的 Ti4+ 后 ,O的 1 s光谱随着 Mg2 + 含量的不同而发生变化 .
SrMg x Ti 1- x O 3 nanocrystalline materials( x =0.1—0.5) were prepared by the stearic acid gel method. Powder samples were characterized by XRD, TG, DAT, IR, XPS and TEM. The results showed that the grain size d changed with the variations of Mg content x , the temperature of calcination and the time of calcination. The result of XPS showed that the binding energy of O 1 s spectra changed with the change of Mg 2+ content after the replacement of Mg 2+ for Ti 4+ .