摘要
A kind of octanol-modifded silica nanoparticle was fabricated and employed as a framework to form‘‘soggy sand’’electrolyte along with 1-butyl-3-methylimidazolium tetrafluoroborate.‘‘Soggy sand’’and poly（vinylidene fluoride-hexafluoropropylene）composite electrolyte membranes were electrospun for the frst time.The properties of this membrane electrolyte have been evaluated by the mechanical test and electrochemical test.The Young’s modulus increased by 275%from 6.8 MPa to 25.5 MPa and the electrical conductivity increased to 7.6 10à5S/cm at 290.15 K when compared to pristine P（VdF-HFP）membrane electrolyte.The conductivity is 3.1 10à4S/cm at 323.15 K.
A kind of octanol-modifded silica nanoparticle was fabricated and employed as a framework to form‘‘soggy sand’’electrolyte along with 1-butyl-3-methylimidazolium tetrafluoroborate.‘‘Soggy sand’’and poly（vinylidene fluoride-hexafluoropropylene）composite electrolyte membranes were electrospun for the frst time.The properties of this membrane electrolyte have been evaluated by the mechanical test and electrochemical test.The Young’s modulus increased by 275%from 6.8 MPa to 25.5 MPa and the electrical conductivity increased to 7.6 10à5S/cm at 290.15 K when compared to pristine P（VdF-HFP）membrane electrolyte.The conductivity is 3.1 10à4S/cm at 323.15 K.
基金
supported by National Key Basic Research Program of China, 973 Program (Nos. 2012CB932800 and 2011CB93570)