锌铝药芯钎焊丝钎焊铝/铜接头性能及组织 被引量:6

Properties and microstructures of the Al/Cu joints brazed by Zn-Al flux cored wires
下载PDF
导出
摘要 采用5种不同成分的锌铝药芯钎焊丝钎焊铝/铜接头,研究钎料成分对接头剪切强度和耐蚀性的影响.研究结果表明:对于同成分的锌铝药芯钎焊丝,采用火焰钎焊的铝/铜接头抗剪强度比炉中钎焊高,Zn80Al20药芯钎焊丝钎焊的铝/铜接头强度最高;随钎料中Al含量降低,铝/铜接头的耐蚀性变差,Zn72Al28药芯钎焊丝钎焊的铝/铜接头耐腐蚀性最好.相同条件下,火焰钎焊铝/铜接头的耐蚀性明显好于炉中钎焊的接头;Zn80Al20药芯钎焊丝钎焊的铝/铜接头钎缝组织呈块状.锌铝药芯钎焊丝中适中的Zn,Al含量有利于使铝/铜接头铜侧界面得到固溶体组织,并避免铝侧母材的过度熔蚀. Five kinds of Zn/Al flux cored wires with different compositions were used to braze Al/Cu joints,and the joints’ shear strengths and corrosion resistances which were affected by compositions were studied. It is shown that for the Zn/Al flux cored wires with the same compositions,the shear strength of the joint brazed by flame brazing is higher than furnace brazing,and the shear strength of the joint brazed by Zn80Al20 flux cored wire is the highest. The corrosion resistance of Al/Cu joint gets worse with the decrease of Al in the solder and that of Al/Cu joint brazed by Zn72Al28 flux cored wire is the best. Under the same conditions,the corrosion resistance of Al/Cu joint brazed by flame brazing is obviously better than furnace brazing and the microstructure of Al/Cu joint brazed by Zn80Al20 flux cored wires is massive. Moderate contents of Zn and Al in the Zn/Al flux cored wire are beneficial to gain solid solution structure in the Cu side of Al/Cu joint and avoid the excessive corrosion of base metal in the side of Al.
出处 《江苏科技大学学报(自然科学版)》 CAS 2013年第5期444-448,共5页 Journal of Jiangsu University of Science and Technology:Natural Science Edition
基金 镇江市国际科技合作项目资助(GJ2010006)
关键词 ZN-AL钎料 药芯钎焊丝 铜接头 剪切强度 微观组织 Zn-Al solder flux cored wire Al/Cu joint shearing strength corrosion resistance
  • 相关文献

参考文献6

二级参考文献16

  • 1苏文英,阎玉芹,叶赐麒.铝-铜火焰钎焊材料研究[J].北京工业大学学报,1994,20(4):45-51. 被引量:18
  • 2张启运.铝及其合金的无腐蚀不溶性钎剂[J].焊接,1995(9):2-3. 被引量:12
  • 3张启运 庄鸿寿.钎焊手册[M].北京:机械工业出版社,1998..
  • 4冲田富晴.Al—Cu系合金の溶接(2)[J].轻金属溶接,1995,33(3):11-18.
  • 5[2]长崎诚三,平林真.二元合金相图[M].北京:冶金工业出版社,2004:48.
  • 6[3]SCHOER H,SCHULTZE W,Process and solder for solde-ring aluminum-containing workpieces:USA,3807033[P].1974-04-30.
  • 7张启运.中温マルミニウムろラ接[J].热处理,1989,29(6):316.
  • 8龙伟民;于新泉;张雷.锌铝药芯钎焊丝的发展及应用展望[A]广西南宁,2008146-149.
  • 9Cooper K P,Jones H N. Microstructural evolution rapidly solidified Al-Cu-Si ternary alloys[J].Journal of Materials Science,2001,(10):70.
  • 10龙伟民,张雷,程亚芳.铝与铜连接技术的研究[J].金属加工(热加工),2008(12):47-49. 被引量:26

共引文献59

同被引文献45

引证文献6

二级引证文献13

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部