薄膜沸腾CVI双热源加热法制备C/C复合材料及其致密化特性 被引量:4

Densification of C/C composites using film boiling chemical vapor infiltration with two heaters
下载PDF
导出
摘要 采用薄膜沸腾CVI以双热源加热的方法在900~12000C下热解二甲苯前驱体增密二维针刺炭毡预制体,30—35h内制备出密度1.70g/cm3~1.73g/cm3的C/C复合材料。研究致密化过程中热解炭基体的沉积速率变化规律,应用排水法和偏光显微镜分别测试材料的密度及热解炭层的厚度。结果表明,当沉积温度由900~1000oC升高至1100~1200oC时,沉积前沿的厚度拓宽,热解炭的初始沉积速率增大,但高沉积温度下预制体边缘将优先完成致密化,导致材料的平均密度由1.72~1.73g/cm降低至1.70,致密化均匀性变差,材料轴向和径向方向的密度偏差高于0.04g/cm3。上热源开多个轴向通孔可使沉积前沿的厚度减小,前驱体在预制体内的传输效率提高,进而改善较高沉积温度下材料的致密化效果。 Two-dimensional needle-punched carbon fiber felts were densified using film boiling chemical vapor infiltration with heat- ers above and below the felt and using xylene pyrolysis at 900-1 200 C. The pyrocarbon deposition rate was calculated from the mass gain of the composites. The density of the composites and the thickness of the pyrocarbon were measured by the Archimedes method and polarized light microscopy, respectively. The effects of deposition temperature and heater configuration on the densification behav- ior of the composites were investigated. Results showed that C/C composites with a density of 1.70-1.73 g/cm3 were produced after 30-35 h densification. The deposition front thickness and initial deposition rate of the pyrocarbon increased with deposition temperature from 900-1 000 ~C to 1 100-1 200 ~(2. However, the difficulty of precursor transfer increased at higher deposition temperatures due to a more rapid densification at the preform edge, leading to a density decrease of the composites from 1.72-1.73 g/cm3 at 900-1 000 ~C and 1 000-1100 ~C to 1.70 g/cm3 at 1 100-1 200 ~(2 if upper heater was not used. Moreover, the densification uniformity of the com- posites decreased, and their density gradients along both the axial and radial directions were larger than 0.04 g/cm3. When the upper heater with many holes along its axial direction was used, the thickness of the deposition front decreased whereas the mass transfer effi- ciency of precursor into the preform increased, which had the advantage of improving the density and uniformity of the composites for the higher deposition temperature of 1 100-1 200 C.
出处 《新型炭材料》 SCIE EI CAS CSCD 北大核心 2013年第6期442-447,共6页 New Carbon Materials
基金 国家自然科学基金(51202233 51002124) 国家'111'引智计划(B08040)~~
关键词 C C复合材料 化学气相渗透 致密化特性 Carbon/carbon composites Chemical vapor infiltration Densification behavior
  • 相关文献

参考文献16

  • 1吴法宇,周艳文,张峻巍,杜金红,李峰.高温处理对螺旋炭纤维微观拓扑结构的影响[J].新型炭材料,2012,27(6):448-454. 被引量:2
  • 2Golecki I. Rapid vapor-phase densification of refractory compos- ites[ J ]. Materials Science and Engineering, 1997, 20 (2) : 37- 124.
  • 3Chen S A, Hu H F, Zhang Y D, et al. Rapid densification of C/ SiC composites by joint processes of CLVD and PIP [ J]. Matteri- als Letters, 2011,65(19-29) : 3137-3139.
  • 4Rovillain D, Trinquecoste M, Bruneton E, et al. Film boiling chemical vapor infiltration: An experimental study on carbon/car- bon composite materials[J]. Carbon, 2001, 39(9) : 1355-1365.
  • 5Delhaes P, Trinquecoste M, Derre A, et al. Film boiling chemical vapor infiltration of C/C composites, influence of mass and ther- mal transfers [J]. Carbon Science, 2003, 4(4) : 1-11.
  • 6李新涛,李克智,李贺军,王鹏云,和永岗.化学液相气化沉积制备的炭/炭复合材料组织均匀性研究[J].固体火箭技术,2007,30(5):437-441. 被引量:3
  • 7Wang J P, Qian J M, Qiao G J, et al. Improvement of film boil- ing chemical vapor infiltration process for fabrication of large size C/C composite[ J]. Materials Letters, 2006, 60 (9-10) : 1269- 1272.
  • 8张永辉,王继平,金志浩.煤油蒸气为前驱体热梯度CVI法制备C/C复合材料[J].新型炭材料,2010,25(2):141-145. 被引量:3
  • 9Feng J Z, Zhang C R, Feng J, et al. Carbon aerogel composites prepared by ambient drying and using oxidized polyacrylonitrile fi- bers as reinforcements [ J ]. ACS Applied Materials & Interfaces, 2011, 3(12) : 4796-4803.
  • 10Nadeau N, Vignoles G L, Brauner C M. Analytical and numeri- cal study of the densification of carbon/carbon composites by a film boiling chemical vapor infiltration process[ J]. Chemical En- gineering Science, 2006, 61(22): 7509-7527.

二级参考文献49

共引文献7

同被引文献36

引证文献4

二级引证文献11

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部