工艺参数对楔横轧螺纹轴心部质量的影响 被引量:2

Effect of process parameters on core quality of thread shaft rolling in cross wedge rolling
原文传递
导出
摘要 楔横轧轧制轧件时,轧件受两向压应力、一向拉应力作用,轧件心部可能产生疏松、裂纹等心部缺陷,采用Deform-3D三维有限元软件模拟了不同工艺参数条件下楔横轧轧制螺纹轴类件的成形过程,从理论上分析了各种工况下轧件内部易产生缺陷的应力应变的变化特点,得出齿高变化率和螺旋升角对轧件心部质量的影响规律。研究结果表明,齿高变化率较大或螺旋升角随螺纹齿形中径尺寸变化时,轧件心部应力、应变都较小。选取合适的工艺参数,螺纹轴内部不会出现心部缺陷。 In cross wedge rolling, rolled pieces are forced by two directions compressive stresses and single direction tensile stress,and the core defects such as core loose and crack and so on could be created. The forming processes of rolling thread shafts in cross wedge rolling were simulated by using Deform-3D in different cases. The variation characteristics of stress and strain for parts which are easily to generate defects in core were theoretically analyzed under various conditions, and the influence rules of change rate of tooth height and helix angle on core quality of rolled pieces were obtained. The results show that when the change rate of tooth height is bigger or the helix angle is selected with the calculated value as the diameter size of thread tooth, the stress and strain in the center of rolled pieces are smaller. No core defects appear inside the thread shaft when selecting appropriate process parameters.
出处 《锻压技术》 CAS CSCD 北大核心 2014年第3期62-66,共5页 Forging & Stamping Technology
基金 河北省自然科学基金资助项目(E2012208066 E2011208014) 河北省教育厅自然科学基金项目(Q2012152) 河北科技大学博士基金项目(QD201001)
关键词 楔横轧 螺纹轴 齿高变化率 螺旋升角 心部缺陷 cross wedge rolling thread shafts change rate of tooth height helix angle core defect
  • 相关文献

参考文献9

二级参考文献32

共引文献55

同被引文献41

引证文献2

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部