组装式离心压缩机腐蚀积垢原因分析及处理措施 被引量:3

Analysis of Assembly Centrifugal Compressor Fouling Corrosion and Prevention
下载PDF
导出
摘要 针对组装式离心空气压缩机积垢、腐蚀、叶轮变形断裂等问题分别进行了分析阐述,首先对叶轮积垢、蜗壳积垢及流道的腐蚀现象做了说明,之后对其形成的原因进行了分析,最终提出相关问题的解决措施。改进的结果使机组运行周期由1 500h延长至8 000h,提高了机组运行的可靠性,延长了压缩机的使用寿命。 This paper specified the fouling, corrosion, deformation of the impeller fracture occurred in assembly centrifugal compressors. Firstly, the impeller fouling, volute fouling and corrosion of flow channel was stated. Then its forming reasons were analyzed. Finally, the solving measures for relevant problems were pointed out. The improved measures extend the unit run cycle from 1500h to 8000h, which improves the reliability of unit operation and extends the using life of compressor.
作者 虞明 朱柏安
出处 《风机技术》 2014年第1期83-86,92,共5页 Chinese Journal of Turbomachinery
关键词 离心空气压缩机 叶轮 积垢 腐蚀 断裂 centrifugal air compressors impeller fouling corrosion fracture
  • 相关文献

参考文献12

二级参考文献29

共引文献91

同被引文献21

引证文献3

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部