The corrosion behavior of 316L stainless steel （31 6L SS） has been investigated in solutions containing various concentrations of chloride ions by using potentiodynamic polarization, capacitance measurement and Mott- Schottky relationship analysis （M-S）. The result indicates that passive currents change slightly with the addition of chloride ions. The pitting potential （Epit） decreases linearly with Iog[CI-]. Correspondingly, the point defect diffusion coefficient （Do） of the passive film increases linearly with increasing Iog[CI-]. The results also indicate that the pitting corrosion of 316L SS follows the adsorption mechanism in NaCI solution.
The corrosion behavior of 316L stainless steel （31 6L SS） has been investigated in solutions containing various concentrations of chloride ions by using potentiodynamic polarization, capacitance measurement and Mott- Schottky relationship analysis （M-S）. The result indicates that passive currents change slightly with the addition of chloride ions. The pitting potential （Epit） decreases linearly with Iog[CI-]. Correspondingly, the point defect diffusion coefficient （Do） of the passive film increases linearly with increasing Iog[CI-]. The results also indicate that the pitting corrosion of 316L SS follows the adsorption mechanism in NaCI solution.
基金
the financial support from the National Natural Science Foundation of China (Nos. 50971050 and 50771038)
the Ministry of Science and Technology of China (No. 2012FY113000)
the Fundamental Research Founds for the Central Universities (No. HEUCF101005).