摘要 改善高碳钢盘条氧化铁皮的剥离率,有助于提高其拉丝成材率。通过扫描电镜显微分析技术研究了高碳钢盘条氧化铁皮剥离后内表面的微观形貌,系统分析了内表面皱褶产生的机理,根据断裂力学理论给出了内表面皱褶起伏的高度和长度与其剥离性能的关系。通过拉伸试验结果与电镜扫描图片对比,研究发现内表面皱褶起伏的高度越小、长度越大就越有利于高碳钢盘条氧化铁皮的剥离。 it would be helpful to improve the yield of wire drawing when the ratio of oxide scale on high carbon steel wire was improved. The morphology of internal surfaces of stripped oxide scale on high carbon steel wire was studied by SEM microscopic analysis, the mechanism of internal surface corrugation was analyzed systematically. The relationships between the stripping performance and the height and length of the corrugation on the internal surface relief were given by fracture mechanics. Comparing the tensile test results with SEM, the conclusion was proved, that height of corrugation of internal surface was the greater and the length was longer, it was more conducive for the stripping performance of oxide scale on high carbon steel wire.
出处 《钢铁》 CAS CSCD 北大核心 2014年第4期76-79,85,共5页 Iron and Steel
关键词 高碳钢盘条 氧化铁皮 内表面 皱褶 剥离性 high carbon steel wire~ oxide scale internal surface corrugation stripping performance
  • 相关文献

参考文献7

二级参考文献28

  • 1林方婷,石旺舟,马学鸣.冷却速率对低碳钢线材表面氧化皮微观结构的影响[J].华东师范大学学报(自然科学版),2006(4):23-28. 被引量:14
  • 2Tomlnaga J, Wakimoto K, Mori T, et al. Manufacture of wire rods with good descaling property[J]. Transactions ISIJ, 1982, 22:646 - 656.
  • 3Confente M, Geneve D, Resiak B, et al. Effects of mechanical descaling on the surface of low carbon wire rod for drawing or cold heading[ J]. Wire Journal International, 1995, 28: 238- 242.
  • 4Parusov V V, Savyuk A N, Sychkov A B, et al. Study of the possibilities for maximizing scale removal from wire rod before drawing[J]. Metallurgist, 2004, 48 : 292 - 297.
  • 5Chen R Y, Yuen W Y D. Review of the high-temperature oxidation of iron and carbon steels in air or oxygen[J]. Oxidation of Metals, 2003, 59 (5/6) :433 - 468.
  • 6Chen R Y, Yuen W Y D. Oxide-scale structures formed on commercial hot-rolled steel strip and their formation mechanisms[J]. Oxidation of Metals, 2001, 56 (1/2) :89- 118.
  • 7Chen R Y, Yuen W Y D. A study of the structure of hot-rolled steel strip by simulated coiling and cooling[ J]. Oxidation of Metals, 2000, 53 (5/6) :539 - 560.
  • 8Sun W H, Tieu A K, Jiang Z Y, et al. High temperature oxide scale characteristic of low carbon steel in hot rolling[J]. Journal of Materials Processing Technology, 2004,155 - 156 : 1307 - 1312.
  • 9Basabe V V, Szpunar J A. Growth rate and phase composition of oxide scale during hot rolling of low carbon steel[ J]. ISIJ International, 2004, 44:1554 - 1559.
  • 10BK-Spec: GA-03-17. Descalability of high carbon wire rod- quick test[S] .2003.

共引文献37

同被引文献29

引证文献4

二级引证文献10

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部