高碳钢150 mm×150 mm连铸坯堆垛缓冷对碳偏析的影响 被引量:4

Effect of 150 mm×150 mm Casting Billet Stacking Slow Cooling Process on Carbon Segregation of High Carbon Steel
下载PDF
导出
摘要 高碳钢SWRH82B(0.81%C)盘条用于生产预应力钢丝钢绞线,其中网状碳化物是造成冷拔断裂的重要原因.试验了该钢150 mm×150 mm铸坯堆垛缓冷时间(0~48 h)对铸坯碳偏析和Φ12.5 mm盘条碳化物的影响.结果表明,直接空冷时的铸坯中碳含量的差值为0.116%,堆垛缓冷12,24,36,48 h后碳含量差值分别降至0.088%,0.080%,0.075%和0.076%,盘条中网状碳化物也相应降低;SWRH82B钢150 mm× 150 mm连铸坯堆垛缓冷24h,可以满足盘条冷拉工艺要求. The coil of high carbon steel SWRH82B (0. 81% C) is used for pre-stressed wire strands, and the serious net carbides in steel is important factor of wire fracture during cold drawing process. The effect of 150 mm×150 mm casting billet stacking slow cooling time (0 -48 h) of steel on carbon segregation in billet and carbide segregation in φ12. 5 mm coil is tested. Results show that the deviation of carbon content in billet with direct air cooling is 0. 116% , after stacking slow cooling of billet for 12, 24, 36 and 48 h, the deviation carbon content in billet respectively decreases to 0. 088% , 0. 080%, 0. 075% and 0. 076%, and the rating of net carbide in coil is also corresponding decreased; it is available to meet the requirement for cold drawing process by stacking slow cooling for 24 h of steel SWRH82B 150 mm × 150 mm cast- ing billet.
出处 《特殊钢》 北大核心 2014年第3期39-41,共3页 Special Steel
关键词 高碳钢SWRH82B 150 mm×150 mm连铸坯 堆垛缓冷 碳偏析 High Carbon Steel SWRH82B, 150 mm × 150 mm Casting Billet, Stacking Slow Cooling, Carbon Segregation
  • 相关文献

参考文献5

二级参考文献17

  • 1Chang Hee Yim, Joong Kil Park, Byong Don You, et al. The Effect of Soft Reduction on Center Segregation in C. C. Slab [J]. ISIJ International, 1996, 36(supplement): s231.
  • 2Yamashita T, Torizuka S, Nagai K. Effect of Manganese Segregation on Fine-Grained Ferrite Structure in Low-Carbon Steel Slabs[J]. ISIJ International, 2003, 43(11):1833.
  • 3Kywng Shik Oh,J K Park ,S H Chang. Development of Soft Reduction Technology for the Bloom Caster at Pohang Works of POSCO[A]. Steelmaking Conference Proceedings[C]. 1995, U. S. A. IRON&STEEL SOCIETY.
  • 4Y Chen,F Feng, K Lin, et al. Improvment of Center Segregation for High Carbon Steel Bloom[A]. Steelmaking Conferece Proceedings[C]. 1996, U. S. A. IRON&STEEL SOCIETY.
  • 5林惠国 付代直.钢的奥氏体转变曲线[M].北京:机械工业出版社,1998..
  • 6殷瑞钰.钢的质量现代进展[M].北京:冶金工业出版社,1995..
  • 7川和高穗 土田裕.连续铸造スヲブの中央偏析の生成机构について[J].铁と钢,1974,60(11):408-408.
  • 8梨和甫 安元邦夫.连铸スヲブの中心偏析に及ぼすロルアヲイメンの影响について[J].铁と钢,1974,60(4):96-96.
  • 9熊井浩 浅野钢一.连铸铁片内の凝固偏析现象と溶钢流动に关系すゐ研究[J].铁と钢,1974,60(7):894-894.
  • 10薛正良,李正邦,张家雯.高碳钢连铸方坯中心偏析[J].炼钢,2000,16(1):56-59. 被引量:42

共引文献94

同被引文献26

引证文献4

二级引证文献27

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部