氧化铝、氮化硅和碳化硅的疲劳特性与寿命预测 被引量:11

FAILURE BEHAVIORS AND LIFETIME PREDICTION OF Al_2O_3, SiC and HP-Si_3N_4
下载PDF
导出
摘要 分析了几种典型的结构陶瓷在长期载荷下的失效特性和差别 .认为长期失效的本质是强度衰减 ,建立了一个疲劳失效的强度衰减模型和提出了寿命预测方法 .分别研究了氧化铝、氮化硅和碳化硅几种常用工程陶瓷在常温和高温下的疲劳特性和差异 .采用三点弯曲的受力方式测试了不同载荷水平下的断裂时间 .结果表明 :碳化硅的疲劳门槛值超过强度的 80 % ,而且受温度影响最小 ;氧化铝的静疲劳受微小裂纹扩展控制 ;氮化硅的高温疲劳主要是蠕变机制导致强度衰减 ,疲劳门槛值不超过强度的 5 0 % .由实验研究了氮化硅的高温静疲劳、动疲劳和循环疲劳三者在相同温度和相同应力峰值条件下的寿命关系 ,结果与计算一致 . Fatigue behavior of three ceramics materials Al2O3, SiC, HP-Si3N4 and their differences were investigated. The study confirmed that the long-term failure of ceramics is due to the strength degradation that can be caused by various factors. A model of strength degradation for failure evaluation is presented and the lifetime calculation can be simplified as a motion equation. Static fatigue behaviors of Al2O3, SiC, HP-Si3N4, and their differences at room temperature and high temperature were investigated experimentally. The lifetimes under different loading levels were measured by means of three-point bending method. The results show that the fatigue threshold of SiC is much higher than that of the other two materials and has no dependence on temperature. The fatigue lifetime of alumina is controlled mainly by the subcritical crack growth, and the fatigue failure of silicon nitride at high temperature is due to the strength degradation caused by creep. The relations between lifetime and loads measured for alumina and silicon nitride are consistent with those predicted by the model of strength degradation. It is found that the data of lifetime of SiC greatly scatter and the fatigue threshold is over 80% of strength. The lifetime relations of Si3N4 under static, cyclic and dynamic fatigue at 1200°C were tested and the results agree well with calculation results.
作者 包亦望
出处 《硅酸盐学报》 EI CAS CSCD 北大核心 2001年第1期21-25,共5页 Journal of The Chinese Ceramic Society
基金 国家自然科学基金资助项目!(5 9872 0 3 5 )
关键词 陶瓷 寿命预测 疲劳特性 强度衰减 氧化铝 氮化硅 碳化硅 Alumina Cracks Fatigue of materials Silicon carbide Silicon nitride Strength of materials
  • 相关文献

参考文献4

  • 1包亦望 金宗哲.陶瓷材料的疲劳表征.第七届断裂学术会议论文集[M].武汉,1993,11..
  • 2邢志强,包亦望,金宗哲,程咏梅,文光芸.热压氮化硅在1200℃的高温疲劳损伤[J].硅酸盐学报,1995,23(1):14-21. 被引量:5
  • 3Bao Yiwang,J Nucl Eng Design,1994年,150卷,323页
  • 4包亦望,第七届全国断裂学术会议论文集,1993年,315页

二级参考文献2

共引文献5

同被引文献121

引证文献11

二级引证文献40

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部