摘要
研究了马尾松硫酸盐浆两段氧脱木质素的最佳工艺条件。结果表明 ,第一段氧脱木质素的条件为 :氧压 0 .6MPa ,温度 10 0℃ ,时间 80min ,NaOH用量 5% ,MgSO4 用量 0 5% ,浆浓 10 % ;第二段氧脱木质素的条件为 :氧压 0 4MPa ,温度 90℃ ,时间 6 0min ,NaOH用量 3% ,MgSO4 用量 0 .5% ,浆浓 10 %。在此条件下 ,OⅠOⅡ 木质素脱除率达到 72 5% ,粘度 775 2cm3 /g ,得率 90 .5%。经过氧脱木质素后浆的裂断长 5.8km ,耐破指数 5.3kPa·m2 /g ,撕裂指数 12 .7mN·m2 /g。
The optimum conditions for two stage delignification of masson pine kraft pulp were studied. The results showed that conditions of the first oxygen delignification stage are: oxygen pressure 0.5 MPa, NaOH charge 5%, MgSO 4 charge 0.5%, cooking at 100 ℃ for 80 min. Conditions of the second oxygen delignification stage are: oxygen pressure 0.4 MPa, NaOH charge 3%, MgSO 4 charge 0.5%,cooking at 90 ℃ for 60 min.Results obtained under these two stages (O ⅠO Ⅱ) are: pulp delignification rate 72.5%, pulp viscosity 775.2 cm 3/g, pulping yield 90.5%, breaking length 5.8 km, endurance index 5.3 kPa·m 2/g, tear index 12.7 mN·m 2/g.
出处
《林产化学与工业》
EI
CAS
CSCD
2001年第1期45-49,共5页
Chemistry and Industry of Forest Products
基金
国家自然科学基金资助项目! (2 980 6 0 0 7)
广东省自然科学基金博士启动资助项目!(974 0 94 )