喷射成形Al-Zn-Mg-Cu系高强铝合金的组织与性能 被引量:37

Structure and property of high strength Al-Zn-Mg-Cu alloy by spray forming
下载PDF
导出
摘要 利用喷射成形工艺制备了Al Zn Mg Cu系高强铝合金材料 ,研究了热挤压工艺与热处理工艺对材料微观组织与力学性能的影响。在峰时效的情况下材料表现出了高的力学性能指标 ,抗拉强度达到 75 4MPa ,屈服强度达到 72 2MPa ,断裂延伸率达到 8% ,与采用传统铸造变形工艺制备的同类合金相比 (σb≥ 6 10MPa,σ0 .2 ≥ 5 80MPa ,δ≥ 4% ) ,性能有了明显的提高。合金性能的提高与其基体中呈弥散分布的Mg7Zn3 相有很大的关系 。 High strength Al Zn Mg Cu alloys were produced by spray forming process. The microstructure and mechanical properties of the extruded products in the T6 and T71 conditions were evaluated. Under peak aged conditions the products exhibit high levels of performance, with tensile strength up to 754 MPa, yield strength to 722 MPa, elongation of 8%, having great improvement compared to the same alloy produced by conventional casting process. The increase in strength is associated with the high volume fraction of Mg 7Zn 3 precipitates. The main hardening mechanism of this alloy is precipitation hardening. [
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2001年第2期279-283,共5页 The Chinese Journal of Nonferrous Metals
基金 国家"八六三"资助项目
关键词 喷射成形 沉淀强化 AL-ZN合金 高强铝合金 组织 性能 spray forming precipitation hardening Al Zn alloy
  • 相关文献

参考文献1

二级参考文献23

共引文献26

同被引文献368

引证文献37

二级引证文献251

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部