热处理制度对一种单晶镍基高温合金γ′相形貌演化的影响 被引量:19

Heat Treatment on the Evolution of γ′ Morphology of A Single Crystal Nickel-base Superalloy
下载PDF
导出
摘要 研究了热处理制度对一种单晶镍基合金γ′相形貌演化的影响。结果表明 :不同的热处理制度对合金的γ′相形貌有很大的影响。合金经固溶处理后 ,γ′相细小弥散析出 ,一次时效处理使γ′相平均尺寸增大 ,一次时效温度在 12 0 0°C以上时 ,由于基体通道变宽 ,有细小的二次γ′相析出 ,二次时效处理对γ′相平均尺寸影响不大 ,只是增加γ′相的正方度。 The influence of heat treatment on the evolution of γ′morphology of a single crystal nickel based superalloy was investigated. The results show that γ′ morphologies have been affected significantly under different heat treatment conditions. Dispersed fine γ′ phase precipitated in the matrix of the alloy during solution heat treatment. The average size of γ′ increased after primary aging treatment. Secondary γ′ phase precipitation was observed when the aging temperature was high above 1200°C as result of matrix channel becoming narrow. No sigificantly changes of the average size of γ′ were seen during secondary aging treatment except the increase of squareness of γ′ phase.
出处 《机械工程材料》 CAS CSCD 北大核心 2001年第4期7-10,共4页 Materials For Mechanical Engineering
关键词 单晶合金 时效 γ′相形貌 热处理制度 镍基高温合金 single crystal superalloy aging treatment γ′ morphology
  • 相关文献

参考文献4

二级参考文献2

  • 1张静华,Metall Trans A,1992年,23卷,1253页
  • 2张静华,1991年

共引文献3

同被引文献144

引证文献19

二级引证文献74

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部