研究了铝热 -离心法制备的铁镍基合金内衬复合钢管的组织结构 ,分析了内衬层沿径向的成分分布。结果表明 ,铁镍合金由奥氏体和铁素体两相组成。铁镍合金内衬层与碳钢基体之间形成了一个宽约2 0 μm的马氏体过渡区。内衬层的成分呈梯度变化 ,合金元素的含量沿径向由内表面到外表面逐渐降低。铝热 -离心法制备的铁镍基合金铝含量较高 ,在内衬层内表面附近铝含量约为 5 %。
The microstructure of the iron-nickel alloy lined layer in a composite pipe produced by centrifugal-thermit process was investigated. The radial composition distribution of the alloying elements in the lined layer was analyzed. The results showed that the iron-nickel alloy was composed of austenite and ferrite. A martensitic transition region of 20 μm in width was formed between the iron-nickel layer and the carbon steel substrate. A concentration gradient of alloying elements was shown in the iron-nickel alloy in the direction of radius of composite pipe. The alloying element contents of the lined layer were higher near the inner surface than near the outside surface in contact with the carbon steel substrate. For example, the aluminum content near the inner surface was 5%.
出处
《粉末冶金技术》
EI
CAS
CSCD
北大核心
2002年第3期162-165,共4页
Powder Metallurgy Technology
关键词
铝热-离心法
铁镍基耐蚀合金
内衬复合钢管
燃烧合成
Austenite
Copper alloys
Corrosion resistant alloys
Iron alloys
Martensitic transformations
Metallographic microstructure