碳酸氢铵沉淀法制备大颗粒球形氧化钇的研究 被引量:13

Study on Preparation of Yttrium Oxide with Large Particle Sizes and Spherical Shapes by Precipitation with Ammonium Bicarbonate
原文传递
导出
摘要 采用碳酸氢铵沉淀法制备球形大颗粒氧化钇粉体,粉体用激光粒度仪、SEM和BET分析方法进行表征,研究了反应温度、料液浓度、陈化时间、灼烧温度对氧化钇形貌、粒度、比表面积的影响。最佳的工艺条件为:沉淀反应温度93℃、料液浓度40 g/L、陈化时间28 h、灼烧温度1400℃,在此条件下制备出氧化钇,中心粒径D50为61.54μm,形貌为针状晶体组成的球形。 Yttrium oxide powder with large particle sizes and spherical shapes were prepared by precipitation with ammonium bicarbonate. The powders were characterizated by laser partical size analyzer,SEM and BET. Influence of reaction temperature,concentration of feed liquid,aging time and calcination temperature on morphology,particle size and specific surface area of yttrium oxide was studied. The optimum process conditions were that the reaction temperature of precipitation was 93℃,concentration of feed liquid was 40 g /L,aging time was 28 h,and calcination temperature was 1400℃. Yttrium oxide with medium diameter of 61. 54μm and acicular spherical morphology was obtained under the conditions.
出处 《稀土》 EI CAS CSCD 北大核心 2014年第3期77-81,共5页 Chinese Rare Earths
关键词 氧化钇 碳酸氢铵 球形 大颗粒 yttrium oxide ammonium bicarbonate spherical shapes larger particle
  • 相关文献

参考文献17

  • 1冀晓鹃,刘建平,任先京,黄新春,周恒.热喷涂用氧化钇球形粉末的制备[J].有色金属(冶炼部分),2008(S1):40-42. 被引量:5
  • 2崔大立,朱兆武,龙志奇,等.一种大粒度大比表面积球形氧化钇的制备方法[P].中国发明专利:CN101381092A,2009-03-11.
  • 3付东兴,刘景辉,徐景杰,等.一种中空球形纳米结构氧化钇稳定氧化锆粉末的制备方法[P].中国发明专利:CN101723683B,2012-06-20.
  • 4于月光,任先京,侯伟骜,等.一种热喷涂用纳米球形氧化钇粉末的制备方法[P].中国发明专利:CN102145913A,2011-08-10.
  • 5Rulison A J, Flagan R C. Synthesis of Yttria powder by eletrospray pyrolysis [J]. Journal of the American Ceram- ic Society, 1994, 77(12) :3244-3250.
  • 6Sharma P K, Jilavi M H, Nab R,et al. Seeding effect in hydrothermal synthesis of nanosize yttria [ J ]. Journal of Materials Science Letters, 1998, 17(10) :823-825.
  • 7刘桂霞,洪广言,王进贤,董相廷.水热法制备具有光滑表面的球形Y_2O_3∶Eu^(3+)发光材料(英文)[J].无机化学学报,2006,22(8):1535-1539. 被引量:8
  • 8廖列文,尹国强,崔英德,何镜泉.均匀沉淀法合成纳米Y_2O_3研究[J].稀土,2005,26(6):41-45. 被引量:10
  • 9Qin X P, Yang H, Zhou G H, et al. Synthesis of submi- cron-sized spherical Y2O3 powder for transparent YAG ceramics[J]. Material Research Bulletin, 2011, 46 (2) : 170-174.
  • 10石生东,任秀莲,魏琦峰.制备碳酸稀土的新方法[P].中国发明专利:CN1070166A,1993-03-24.

二级参考文献60

共引文献128

同被引文献235

引证文献13

二级引证文献80

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部