摘要
通过极化曲线测试、浸泡实验和表面分析技术研究了不同交流电流密度对X65钢在碳酸盐/碳酸氢盐溶液中腐蚀行为的影响.随交流电流密度的增加,钝化区宽度明显变窄,点蚀击破电位负移,维钝电流密度增大,腐蚀速率增加.在低交流电流密度下(<100A·m-2),维钝电流密度、点蚀程度和腐蚀速率均略增加;在高交流电流密度下(≥100A·m-2),维钝电流密度、点蚀程度和腐蚀速率均快速增加.
The effects of AC current density on the corrosion behavior of X65 steel in concentrated carbonate /bicarbonate solutions were studied by potentiodynamic polarization curve measurement,immersion testing and the surface characterization technique. When the AC current density increases,the passive region significantly narrows,the pitting potential negatively shifts,the passive current density increases,and the corrosion of X65 steel accelerates. At low AC current density（ 100 A·m^-2） the passive current density,the pitting corrosion degree and the corrosion rate slightly increase with the increasing of AC current density,but at high AC current density（ ≥100 A·m^-2）,they increase rapidly.
出处
《北京科技大学学报》
EI
CAS
CSCD
北大核心
2014年第8期1077-1081,共5页
Journal of University of Science and Technology Beijing
基金
国家自然科学基金资助项目(51371036
51131001)
关键词
钢腐蚀
交流电场
电流密度
碳酸盐
碳酸氢盐
腐蚀速率
steel corrosion
AC electric field
current density
carbonates
bicarbonates
corrosion rate