Austenite Grain Refinement and Isothermal Growth Behavior in a Low Carbon Vanadium Microalloyed Steel 被引量:24

Austenite Grain Refinement and Isothermal Growth Behavior in a Low Carbon Vanadium Microalloyed Steel
原文传递
导出
摘要 The austenite grain refinement through control of the grain growth during reheating process after thermomechanical controlled process (TMCP) in a vanadium microalloyed steel was achieved. The formation of ultra-fine grained austenite was attributed to the high density of austenite nucleation at the ferrite/martensite structure and to the inhibition of austenite growth by (Ti~ V)C particles at the relatively low reheating temperature. Corresponding with the precipitation behavior of (Ti,V)C with temperature, the growth behavior of austenite in the vanadium mi- croalloyed steel could be divided into two regions. At lower reheating temperature, austenite grains grew slowly, and ultra-fine grained austenite smaller than 5 ~m was successfully obtained. By contrast, the austenite grains grew rap- idly at high temperature due to the dissolution of (Ti, V)C particles. According to the measured and predicted results of austenite growth kinetics, two models were developed to describe the growth behavior of austenite grains in two different temperature regions, and the apparent activation energy Qapp for grain growth was estimated to be about 115 and 195 kJ/mol, respectively. The austenite grain refinement through control of the grain growth during reheating process after thermomechanical controlled process (TMCP) in a vanadium microalloyed steel was achieved. The formation of ultra-fine grained austenite was attributed to the high density of austenite nucleation at the ferrite/martensite structure and to the inhibition of austenite growth by (Ti~ V)C particles at the relatively low reheating temperature. Corresponding with the precipitation behavior of (Ti,V)C with temperature, the growth behavior of austenite in the vanadium mi- croalloyed steel could be divided into two regions. At lower reheating temperature, austenite grains grew slowly, and ultra-fine grained austenite smaller than 5 ~m was successfully obtained. By contrast, the austenite grains grew rap- idly at high temperature due to the dissolution of (Ti, V)C particles. According to the measured and predicted results of austenite growth kinetics, two models were developed to describe the growth behavior of austenite grains in two different temperature regions, and the apparent activation energy Qapp for grain growth was estimated to be about 115 and 195 kJ/mol, respectively.
出处 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2014年第8期757-764,共8页
基金 Item Sponsored by National Basic Research Program of China(2010CB630805) National Natural Science Foundation of China(51201036) China Iron and Steel Research Institute Group(12060840A)
关键词 grain refinement austenization (Ti V) C precipitationl grain growth AUSTENITE grain refinement austenization (Ti, V) C precipitationl grain growth austenite
  • 相关文献

参考文献20

  • 1W. Yu. Y. J. Qian , H. B. Wu, Y. H. Yang. 1. Iron Steel Res. Int. 18 (2011) No.2, 64-69.
  • 2J. Y. Yoo. W. Y. Chao. T. W. Park. Y. W. Kim. lSI] Int. 35 (1995) 1034-1040.
  • 3C. Ouchi , lSI] Int. 41 (2001) 542-553.
  • 4S. K. Dhua , S. K. Sen. Mater. Sci. Eng. A 528 (2011) 6356- 6365.
  • 5M. Zhou, LX. r?. X. H. Liu , J. Iron Steel Res. Int. 18 (2011) No.3, 59-64.
  • 6A K. Giumelli , M. Militzer , E. B. Hawbolt , lSI] Int. 39 (1999) 271-280.
  • 7S. Jiao. J. Penning. F. Leysen , Y. Houbaert , E. Aernoudt , lSI] Int. 40 (2000) 1035-1040.
  • 8S.1. Lee. Y. K. Lee. Mater. Des. 29 (2008) 1840-1844.
  • 9S. S. Zhang. M. Q. Li. Y. G. Liu , J. Luo. T. G. u?. Mater. Sci. Eng. A 528 (2011) 4967-4972.
  • 10S. J. Yao. L. X. Du. X. H. Liu , G. D. Wang. J. Mater. Sci. Techno!. 25 (2009) 615-618.

同被引文献171

引证文献24

二级引证文献92

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部