摘要
采用改性环氧配套衬里的方案制备防腐蚀层。对普通混凝土试样与陶粒砼试样及防腐蚀层在脱硫系统烟道内的现场腐蚀行为进行试验研究。试验6个月后环氧配套衬里层没有鼓泡烧蚀,未观察到明显的变化。采用环氧配套衬里防腐蚀层的混凝土试块,在试验6个月后其内部的钢筋未发现腐蚀现象,表明环氧配套衬里对混凝土中的钢筋起到了较好的保护作用。试验6个月后环氧配套衬里混凝土样的能谱结果均未检测到氯元素,硫元素的含量同未试验的对比测试样相比也未增加,表明环氧配套衬里对混凝土起到了很好的保护作用。工程应用结果表明,改性环氧配套衬里的防腐蚀方案能够对湿法脱硫系统的混凝土烟道起到很好的防腐蚀保护作用。
The corrosion behavior of bare common concrete,bare ceramsite concrete and test blocks with modified epoxy liner anticorrosion coating was studied in concrete chimney of flue gas desulphurization systems.Blister of the coating and other obvious changes did not appear on the epoxy liners after 6 months test.No any corrosion indication happened to the rebar in concrete block with epoxy liner anticorrosion coating,indicating a good protection to the rebar in concrete block.After 6 months test,the chlorine element in concrete block with epoxy liners was not found by the analysis result of energy dispersive spectrometer,and the content of sulfur did not increase compared with the untested concrete block.The results showed that the epoxy liner anticorrosion coating could prevent the permeation of harmful corrosives and provide the concrete block with very good protection.The results of engineering application experiment also proved the very good protection of epoxy liner anticorrosion scheme for concrete chimney in flue gas desulphurization systems.
出处
《腐蚀与防护》
CAS
北大核心
2014年第11期1152-1155,共4页
Corrosion & Protection
关键词
脱硫
烟气
混凝土
防腐蚀
改性环氧配套衬里
desulphurization
flue gas
concrete
anticorrosion
modified epoxy liner