摘要
本文研究了含硅铬铁矿粉在碱度1.60～1.80的条件下微波加热体还原物料的显微矿相结构。在温度1100℃、1200℃、1300℃（大气压且无保护气氛）时，含硅铬铁粉矿在微波冶炼条件下的显微矿相结构以热碎裂还原结构以及铬铁矿粉颗粒周围渣相结构为主，随着冶炼温度的提高热碎裂也逐渐加剧。被还原的铬铁矿颗粒表面由最初边缘到内部的细小热碎裂还原结构扩展到最后的完全崩裂结构，且CrFe金属相中铬、铁含量也随着冶炼温度的提高而增加。最终在1300℃时实现渣金相完全分离。
The microstructure of voluminal reduction on chromite ore fines containing silicon （ basicity：1.60 ~1.80 ） heated by microwave was studied in the paper. At the temperature of 1 100 ℃, 1 200 ℃ and 1 300 ℃ （ at atmospheric pressure without protective gas） , the microstructure of voluminal reduction on chromite ore fines containing silicon heated by microwave consisted mainly of the thermic fractured reduction structure from the edge to inside at the first. The fines thermic fractured reduction structures were dominated by the increase of temperature. Finally, at the temperature of 1300 ℃, complete separation occured, and Fe,Cr content in metallic CrFe phase increased with temperature.
出处
《电子显微学报》
CAS
CSCD
2014年第6期526-530,共5页
Journal of Chinese Electron Microscopy Society
基金
云南科技创新人才计划资助项目(No.2013HA002)
关键词
微波加热
含硅铬铁矿粉
显微矿相结构
microwave heating chromite ore fines containing silicon microstructure