800 MPa级钛铌析出强化高强钢焊接接头的组织与力学性能 被引量:8

Microstructure and Mechanical Properties of Welded Joints of 800 MPa High Strength Steels with Ti and Nb Precipitation Strengthening
下载PDF
导出
摘要 采用混合气体保护焊,在13kJ·cm-1热输入下对3种不同钼、硼含量的800MPa级钛铌析出强化高强钢进行焊接试验,并对焊接接头的组织、强度及硬度进行研究。结果表明:低钼含量高强钢存在热影响区软化现象;随着淬透性元素钼和硼的添加,焊接热影响区的硬度增大,抗拉强度由720 MPa分别增至760 MPa和795 MPa;钼和硼元素的添加对(Ti,Nb,Mo)(C,N)第二相粒子在热影响区的行为没有显著影响。 Three kinds of 800 MPa high strength steels with Ti and Nb precipitation strengthening and containing different Mo and B contents were weld under the conditions of mixed gas arc welding and heat input of13kJ·cm-1,and the microstructure,strength and hardness of the welded joints were studied.The results show that the heat affected zone(HAZ)of the high strength steel with lower Mo was found softening.With the increasing of Mo and B,which increased the hardenability characteristic,the hardness of HAZ increased and the tensile strength increased from 720 MPa to 760 MPa and 795 MPa,respectively.Adding Mo and B elements had no obvious affection on the behavior of second phase particle(Ti,Nb,Mo)(C,N)in HAZ.
机构地区 首钢技术研究院
出处 《机械工程材料》 CAS CSCD 北大核心 2014年第11期21-25,共5页 Materials For Mechanical Engineering
关键词 钛铌析出强化 高强钢 接头强度 HAZ硬度 第二相粒子 precipitation strengthing with Ti and Nb high strength steel strength of welded joint hardness of HAZ second phase particle
  • 相关文献

参考文献3

二级参考文献21

  • 1布赖恩匹克林F.钢的组织与性能[M].北京:科学出版社,1999.278-281.
  • 2Joch J, Ainsworth R A, Hyde T H. Limit load and Jestimates for idealized problem of deeply cracked welding joints in plane strain bending and tension [ J ]. Fatigue Fract.engng.Mater.struct, 1993, 16 (10): 1061~1097.
  • 3Lei Y, Ainsworth R A. A J-integral estimation method for cracks in welds with mismatched mechanical properties [ J ].Int. J. of Pressure Vessels and Piping, 1997, 70 (3):237 -245.
  • 4Toyeda M, Mochizuki M, Shintomi T, et al. Analytical study on deformation and strength in HAZ softened weld joints of fine-grained steels [ A ]. The 54th annual assembly of the international institute of welding [ C ]. ⅡW Doc. Ⅹ-1503-2002.
  • 5马维甸 田锡唐.低匹配焊接接头不均匀裂微体的J积分研究[J].焊接学报,1987,8(2):82-97.
  • 6JOONOH M. JONGBONGL, CHANGHEE L. Predition for the austenite grain size in the presence of growing particles in the weld HAZ of Ti microalloyed steel[J]. Materials Science and Engineering A, 2007,159( 1 / 2) :10-46.
  • 7AKSEI.SEN O M.GRONG O, RYUM N. et al. HAZ grain growth mechanisms in welding of low carbon mieroalloyed stees[J]. Acta Metallurgica,1986,34(9):1807-1815.
  • 8JOONOH M, CHANGHHEE L. Behavior of (Ti,Nb) (C,N) complex particle during thermomechanical cycling in lhe weld CGHAZ of a microalloyed steel[J]. Acta Materialia,2009,57(7):2311-2320.
  • 9WANG X M, HE X I, YANG S W, et al. Refining of intermediate transformation microstructure by relaxation processing [J]. IAIIJ Int ,2002,42( 19 ) : 1553-1559.
  • 10Joonoh M, Changhee L. Behavior of(Ti, Nb)(C, N) complex particle during thermomechmfical cycling in the weld CGHAZ of a micro-alloyed steel[ J ]. Acta Materialia, 2009, 57 : 2311 - 2320.

共引文献83

同被引文献87

引证文献8

二级引证文献32

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部