The effects of vacuum assistance on the microstructure and mechanical properties of high-pressure die cast AZ91 D alloy at different slow shot speeds were evaluated. Plate-shaped castings of AZ91 D alloy were carried out on a TOYO BD-350V5 cold chamber die casting machine incorporated with a self-improved TOYO vacuum system. It was found that the vacuum pressure in the die cavity at the beginning of mold filling increases with the increase of slow shot speed, following a cubic polynomial curve, resulting in a decline in the porosity-reduction ability of vacuum assistance with the increase of slow shot speed. The externally solidified crystal（ESC） contents in conventional and vacuum die castings behave similar against the slow shot speed. The tensile properties of vacuum die castings were strongly influenced by the ESC content at relative low slow shot speeds. With the increase of slow shot speed, the influence of the gas porosity level in vacuum die castings would get prominent.
对不同慢压射速度条件下真空辅助对AZ91D镁合金压铸件组织及力学性能的影响进行了评估。在联合有自行改进的TOYO真空系统的TOYO BD-350V5型冷室压铸机上制备片状AZ91D镁合金压铸件。研究发现,充型时型腔真空压力随着慢压射速度的升高呈现3次方增长,导致真空辅助对压铸件中气孔的降低能力随着慢压射速度的降低而下降。常规和真空压铸件中压室预结晶组织(ESC)含量随着慢压射速度的变化趋势相似。在较低慢压射速度时,真空压铸件拉伸性能受ESC含量的影响很大,随着慢压射速度的升高,真空压铸件中气孔含量的影响将变得显著。
基金
Project(2012ZX04012011)supported by the National Science and Technology Major Project of the Ministry of Science and Technology of China
Project(2011BAE22B02)supported by the National Key Technologies R&D Program of China
Project(51275269)supported by the National Natural Science Foundation of China